ESTIMATION OF DELAYED FRACTURE PROPERTY OF STEELS

被引：60

作者：

SUZUKI, N

ISHII, N

MIYAGAWA, T

HARADA, H

机构：

[1] NIPPON STEEL CORP LTD,R&D LABS 2,KITAKYUSHU 805,JAPAN

[2] NIPPON STEEL CORP LTD,DIV BAR SHAPE & WIRE ROD TECH,CHIYODA KU,TOKYO 10071,JAPAN

来源：

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1993年 / 79卷 / 02期

关键词：

HYDROGEN MEASUREMENT; DELAYED FRACTURE ESTIMATION; CRITICAL HYDROGEN LEVEL;

D O I：

10.2355/tetsutohagane1955.79.2_227

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A new testing method was developed which enables to quantify minute amount of hydrogen in steel and measure resistance of steel to delayed fracture. This method clarified a steel had critical hydrogen level (H(T)) for delayed fracture under a constant applied load. Based on this testing method, a new approach for estimating delayed fracture of steel in service was proposed. From the value of H(T) obtained by this testing method, together with amount of hydrogen absorbed in the steel in a service environment, which is measured by a hydrogen monitoring device, delayed fracture of steel in service can be estimated.

引用

页码：227 / 232

页数：6

共 7 条

[1]

Irwin GR., 1957, J APPL MECH, V24, P361, DOI [10.1115/1.4011547, DOI 10.1111/J.1460-2695.2012.01707.X]

[2]

JOHNSON HH, 1958, T AM I MIN MET ENG, V212, P528

[3] HYDROGEN TRAPPING IN AISI-4340 STEEL [J].

LEE, JL ;

LEE, JY .

METAL SCIENCE, 1983, 17 (09) :426-432

[4]

OTSUBO T, 1979, 2ND P JIM INT S HYDR, P241

[5]

STEIGERWALD EA, 1959, T AM I MIN MET ENG, V215, P1048

[6]

SUZUKI N, 1986, WIRE J INT, V11, P36

[7] HYDROGEN ASSISTED CRACKING IN C-MN AND LOW-ALLOY STEEL WELDMENTS [J].

YURIOKA, N ;

SUZUKI, H .

INTERNATIONAL MATERIALS REVIEWS, 1990, 35 (04) :217-249

← 1 →