INFLUENCE OF NONMETALLIC INCLUSIONS ON CONTACT FATIGUE DEFECTS IN ZIRCONIUM CONTAINING RAILS

被引：0

作者：

DOBUZHSKAYA, AB ^{[1
]}

REIKHART, VA ^{[1
]}

SYREISHCHIKOVA, VI ^{[1
]}

VELIKANOV, AV ^{[1
]}

KOSHINA, IV ^{[1
]}

机构：

[1] ALL UNION RAILWAY TRANSPORT RES INST,MOSCOW,USSR

来源：

STEEL IN THE USSR | 1990年 / 20卷 / 11期

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Investigations were carried out on trial batches of zirconium containing rails to establish the influence of non-metallic inclusions formed in rail steel deoxidised with complex alloys on contact fatigue damage to rails. The morphology, nature, and distribution of inclusions were studied on microsections taken from rails before and after tests. Metallographic, electron probe, and chemical methods were used, and petrographic data were referred to. The mechanical properties of rails were determined in static tensile tests and in impact bending tests. No correlation was found between mechanical properties and contact fatigue defects in rails of the trial batches.

引用

页码：561 / 564

页数：4

共 50 条

[31] INFLUENCE OF NONMETALLIC INCLUSIONS ON VISCOSITY OF MOLTEN STEEL
ARKHAROV, VI
YERSHOV, GS
NOVOKHAT.IA
PHYSICS OF METALS AND METALLOGRAPHY-USSR, 1971, 31 (03): : 217 - &
[32] Effect of Nonmetallic Inclusions, Gases, and Undesirable Accompanying Elements on the Failure Susceptibility of Rails.
Masin, Alois
Hutnicke listy, 1983, 38 (02): : 81 - 88
[33] ONE OF CAUSES OF CONTACT FATIGUE FRACTURE OF RAILS
LUKYANOV, AV
STAL IN ENGLISH-USSR, 1970, (04): : 292 - &
[34] NONMETALLIC INCLUSIONS AND AUSTENITE GRAINS OF STEEL CONTAINING TELLURIUM
POPOVA, LV
NASIBOV, AG
GULEI, GG
SVESHNIKOVA, GA
METAL SCIENCE AND HEAT TREATMENT, 1986, 28 (1-2) : 52 - 55
[35] Prediction of Life and Scatter of Fatigue Failure originated at nonmetallic Inclusions
Murakami, Yukitaka
Yamashita, Yoichi
XVII INTERNATIONAL COLLOQUIUM ON MECHANICAL FATIGUE OF METALS (ICMFM17), 2014, 74 : 6 - 11
[36] THE INFLUENCE OF MACHINING DEFECTS AND INCLUSIONS ON THE FATIGUE PROPERTIES OF A HARDENED SPRING STEEL
BERGENGREN, Y
LARSSON, M
MELANDER, A
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (10) : 1071 - 1087
[37] Influence of machining defects and inclusions on the fatigue properties of a hardened spring steel
Bergengren, Y.
Larsson, M.
Melander, A.
Fatigue and Fracture of Engineering Materials and Structures, 1995, 18 (10) : 1071 - 1087
[38] Rolling contact fatigue analysis of rails under the influence of residual stresses induced by manufacturing
Nejad, R. Masoudi
Shariati, M.
Farhangdoost, Kh
Atrian, A.
SCIENTIA IRANICA, 2019, 26 (03) : 1427 - 1437
[39] Investigation of the Effect of the Strength of Railroad Rails on the Formation of Contact-Fatigue Defects During Use.
Lempitskii, V.V.
Kazarnovskii, D.S.
Shnaperman, L.Ya.
1600, (07):
[40] Influence of Nonmetallic Inclusions on the Failure of Cast Stainless Steels
Fomicheva N.B.
Markova E.V.
Steel in Translation, 2019, 49 (03): : 207 - 211

← 1 2 3 4 5 →