EFFECTS OF HIGH-TEMPERATURE AUSTENITIZATION ON FRACTURE, FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS .2. FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR

被引：3

作者：

CAO, WD ^{[1
]}

LU, XP ^{[1
]}

机构：

[1] TSINGHUA UNIV,DEPT MECH ENGN,BEIJING,PEOPLES R CHINA

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1989年 / 110卷

关键词：

D O I：

10.1016/0921-5093(89)90167-6

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

引用

页码：165 / 174

页数：10

共 31 条

[1] Andrew R. C., 1979, Metal Science, V13, P78
[2] INTERGRANULAR FRACTURE IN 4340-TYPE STEELS - EFFECTS OF IMPURITIES AND HYDROGEN
BANERJI, SK
MCMAHON, CJ
FENG, HC
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (02): : 237 - 247
[3] BANERJI SK, 1977, MECH ENV SENSITIVE C, P437
[4] HYDROGEN PERMEABILITY AND DELAYED FAILURE OF POLARIZED MARTENSTIC STEELS
BARTH, CF
STEIGERW.EA
TROIANO, AR
[J]. CORROSION, 1969, 25 (09) : 353 - &
[5] BEEVERS CJ, 1986, FATIGUE CRACK GROWTH, P89
[6] A COMPARATIVE-STUDY OF MONOTONIC FRACTURE, ENVIRONMENTALLY ASSISTED FRACTURE AND FATIGUE BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS
CAO, WD
LU, XP
LIU, JJ
YANG, AD
[J]. MATERIALS SCIENCE AND ENGINEERING, 1984, 63 (02): : 165 - 187
[7] EFFECTS OF HIGH-TEMPERATURE AUSTENITIZATION ON FRACTURE, FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS .1. MONOTONIC FRACTURE-BEHAVIOR
CAO, WD
LU, XP
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 110 : 151 - 164
[8] EFFECT OF PRIOR AUSTENITE GRAIN-SIZE ON NEAR-THRESHOLD FATIGUE CRACK GROWTH
CARLSON, MF
RITCHIE, RO
[J]. SCRIPTA METALLURGICA, 1977, 11 (12): : 1113 - 1118
[9] EFFECT OF SILICON ON STRESS CORROSION RESISTANCE OF LOW ALLOY HIGH STRENGTH STEELS
CARTER, CS
[J]. CORROSION, 1969, 25 (10) : 423 - &
[10] CRACK PATHS AND HYDROGEN-ASSISTED CRACK-GROWTH RESPONSE IN AISI-4340 STEEL
GAO, M
LU, M
WEI, RP
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (04): : 735 - 746

← 1 2 3 4 →