EQUILIBRIUM PHASE DIAGRAM OF LITHIUM FLUORIDE-BERYLLIUM FLUORIDE-ZIRCONIUM FLUORIDE SYSTEM

The equilibrium phase diagram for the LiF-BeF2-ZrF4 system was established throughout all temperature intervals (approximately 350 to 1000 °C) in which liquid-solid phase transitions occur. The liquidus surface of the LiF-BeF2-ZrF4 system comprises eight primary phase fields, those of the three components, and of five complex compounds: Li2BeF4 Li3ZrF7, Li2ZrF6, Li3Zr4F19, and Li6BeF4ZrF8. The associated phase reactions result in the occurrence of nine invariant equilibrium points, at temperatures which range from 355 to 540 °C. A region of liquid-liquid immiscibility, rare in fluoride systems, was observed with BeF2-rich mixtures at temperatures from the LiF-BeF2-ZrF4 liquidus to an upper critical solution temperature of 955 °C. Composition-temperature relationships within this region were established by use of a high-temperature centrifuge. Le diagramme de constitution du système LiF-BeF2-ZrF4 a été établi sur le domaine de température d'environ 350 à 1000 °C, intervalle dans lequel se produisent les changements de phase liquide-solide. La surface du liquidus du système LiF-BeF2-ZrF4 comprend 8 domaines de phases primaires, ceux de 3 composants et ceux de 5 composés complexes: Li2BeF4, Li3ZrF7, Li2ZrF6, Li3Zr4F19, et Li6BeF4ZrF8. Les réactions de phases associées à ces composés ont pour résultat la production de 9 points d'équilibre invariant à des températures qui s'échelonnent de 355° à 540 °C. Une région d'immiscibilité dans la phase liquide, rare dans les systèmes à base de fluorure, a été observée avec les mélanges riches en BeF2 aux températures comprises depuis le liquidus LiF-BeF2-ZrF4 jusqu'à une température supérieure de mise en solution critique de 955 °C. Les relations entre composition et température dans cette région ont étéétablies en utilisant une centrifugeuse à haute température. © 1968.