TARNISHING OF AU-AG-CU ALLOY STUDIED BY AUGER-ELECTRON SPECTROSCOPY AND COULOMETRY

被引：0
作者：
COURTY, C
MATHIEU, HJ
LANDOLT, D
机构：
来源：
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION | 1991年 / 42卷 / 06期
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Tarnishing of a single phase 14 carats Au-Ag-Cu alloy was studied using the Tuccillo-Nielsen test. Auger Electron Spectroscopy and coulometry were employed for the characterization of the composition and the thickness of the surface layers formed. X-ray diffraction was used for further characterization of thicker layers. The layer formation followed linear kinetics. The tarnished layer at short test durations of 0.5 to 5 hours consisted mainly of Ag2S, CuS and Cu2S or compounds near to this stoichiometry. The composition of the top surface of the tarnished layer is constant but its global composition changes with the duration of the tarnishing test.
引用
收藏
页码：288 / 295
页数：8
相关论文
共 16 条
[1]   INFLUENCE OF SURFACE STRUCTURE ON TARNISHING REACTION [J].
ALLPRESS, JG ;
SANDERS, JV .
PHILOSOPHICAL MAGAZINE, 1964, 10 (107) :827-&
[2]  
Bard A. J, 1985, STANDARD POTENTIALS
[3]   A CRITIQUE OF THE TUCCILLO-NIELSEN WHEEL METHOD FOR TARNISH TESTING OF DENTAL ALLOYS [J].
CHANA, MS ;
KUHN, AT .
JOURNAL OF DENTISTRY, 1984, 12 (04) :314-318
[4]   A THERMODYNAMIC PERSPECTIVE OF COPPER TARNISHING IN MOIST AIR-SO2 [J].
CHAWLA, SK ;
PAYER, JH .
CORROSION, 1990, 46 (10) :860-865
[5]  
ELDIN AMS, 1985, ELECTROCHIM ACTA, V30, P461
[6]  
FRITZ JW, 1988, THESIS PENNSYLVANIA
[7]  
GUINEMENT J, 1986, 13 INT C EL CONT LAU, P383
[8]   TARNISHING AND STRUCTURES OF SOME ANNEALED DENTAL LOW-GOLD ALLOYS [J].
HERO, H .
JOURNAL OF DENTAL RESEARCH, 1984, 63 (06) :926-931
[9]   ANODIC-DISSOLUTION OF BINARY SINGLE-PHASE ALLOYS AT SUBCRITICAL POTENTIAL [J].
LAURENT, J ;
LANDOLT, D .
ELECTROCHIMICA ACTA, 1991, 36 (01) :49-58
[10]   TRANSFER AND TREATMENT OF AES, XPS AND SIMS DATA WITH A NETWORK COMPUTER STATION [J].
MATHIEU, HJ ;
MISCHLER, S ;
VOGEL, A ;
SEILER, A ;
RIEDL, G .
SURFACE AND INTERFACE ANALYSIS, 1988, 12 (1-12) :78-82
12