HYDRO-ABRASIVE EROSION CHARACTERISTICS OF 30VOL-PERCENT-SICP/6061-T6 AL COMPOSITE AT SHALLOW IMPACT ANGLES

被引：36
作者：
RAMULU, M
RAJU, SP
INOUE, H
ZENG, J
机构：
[1] UNIV OSAKA PREFECTURE,DEPT MECH ENGN,OSAKA 591,JAPAN
[2] UNIV RHODE ISL,DEPT MECH ENGN,KINGSTON,RI 02881
来源：
WEAR | 1993年 / 166卷 / 01期
基金：
美国国家科学基金会;
关键词：
D O I：
10.1016/0043-1648(93)90279-U
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Hydro-abrasive erosion characteristics were investigated for 30vol.%SiC(p)/6061-T6 Al composite material and 6061-T6 aluminium alloy at steady-state conditions using abrasive waterjets. The erosion rates were measured for shallow impact angles (<20-degrees) and the influence of the abrasive size, flow rate and the impact angle on the erosion process was studied. Scanning electron microscopy (SEM) was used to characterize the eroded surface and the results showed that erosion in the composite occurred due to microcutting of the aluminium matrix material, with the SiC particulates being removed subsequently by the shovelling action of the oncoming jet. The experiments also revealed that the erosive wear rates for the 30vol.%SiC(p)/6061-T6 Al composite were less than the erosive wear rates of the 6061-T6 aluminium alloy by a factor of two.
引用
收藏
页码：55 / 63
页数：9
相关论文
共 23 条
[1]  
BENCHAITA MT, 1980, THESIS MIT CAMBRIDGE
[2]  
Bitter J. G. A., 1963, WEAR, V6, P169, DOI [10.1016/0043-1648(63)90073-5, DOI 10.1016/0043-1648(63)90073-5]
[3]  
Bitter J. G. A., 1963, WEAR, V6, P5, DOI [10.1016/0043-1648(63)90003-6, DOI 10.1016/0043-1648(63)90003-6, 10.1016/]
[4]  
DAIMARU A, 1985, ASTM STP, V864, P505
[5]  
FADDICK RR, 1975, 1ST I C INT EXT PROT
[6]   VELOCITY DEPENDENCE OF EROSION OF DUCTILE METALS BY SOLID PARTICLES AT LOW ANGLES OF INCIDENCE [J].
FINNIE, I ;
MCFADDEN, DH .
WEAR, 1978, 48 (01) :181-190
[7]  
FINNIE I, 1961, ASTM STP, V307, P70
[8]  
Finnie I., 1960, WEAR, V3, P87, DOI [DOI 10.1016/0043-1648(60)90055-7, 10.1016/00431648(60)90055-7]
[9]  
GORETTA KC, 1990, TRIBOLOGY OF COMPOSITE MATERIALS, P147
[10]  
HALLOWELL JB, 1986, STRUCTURAL ALLOYS HD, V3
123