INFRARED LATTICE-VIBRATIONS IN NAGAO2

被引：2

作者：

SOBOTTA, H ^{[1
]}

NEUMANN, H ^{[1
]}

SCHUMANN, B ^{[1
]}

KUHN, G ^{[1
]}

RIEDE, V ^{[1
]}

机构：

[1] UNIV LEIPZIG,INST KRISTALLOG & MATERIALWISSENSCH,SEKT CHEM,O-7030 LEIPZIG,GERMANY

来源：

CRYSTAL RESEARCH AND TECHNOLOGY | 1991年 / 26卷 / 06期

关键词：

D O I：

10.1002/crat.2170260612

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

Infrared reflectivity spectra of NaGaO2 samples prepared from powdered material are measured at room temperature in the wavenumber range from 180 to 4000 cm-1. An analysis of the spectra with the Kramers-Kronig method reveals 16 vibrational modes. From a comparison of the results for NaGaO2 with previous measurements on the isostructural compound LiGaO2 conclusions are made with regard to the Ga-O and Na-O bond related vibrational modes.

引用

页码：735 / 738

页数：4

共 5 条

[1] RAMAN-SPECTRA AND VALENCE FORCE-FIELD OF SINGLE-CRYSTALLINE BETA-GA2O3 [J].

DOHY, D ;

LUCAZEAU, G ;

REVCOLEVSCHI, A .

JOURNAL OF SOLID STATE CHEMISTRY, 1982, 45 (02) :180-192

[2]

HOPPE R, 1965, B SOC CHIM FR, P1115

[3] COMPARATIVE INFRARED LATTICE VIBRATION STUDY OF LIGAO2 AND LIINO2 .2. INTERATOMIC FORCE-CONSTANTS [J].

NEUMANN, H .

CRYSTAL RESEARCH AND TECHNOLOGY, 1990, 25 (06) :667-675

[4] COMPARATIVE INFRARED LATTICE VIBRATION STUDY OF LIGAO2 AND LI1NO2 .1. EXPERIMENTAL RESULTS [J].

SOBOTTA, H ;

KUHN, G ;

NEUMANN, H ;

RIEDE, V .

CRYSTAL RESEARCH AND TECHNOLOGY, 1989, 24 (04) :459-465

[5] OXOGALLATES OF ALKALI METALS [J].

VIELHABER, E ;

HOPPE, R .

ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1969, 369 (1-2) :14-+

← 1 →