INVESTIGATIONS OF BOSWELLIA GLABRA ELECTRET

被引:11
作者
PILLAI, PKC
JAIN, VK
机构
[1] Department of Physics, Indian Institute of Technology, Delhi, New Delhi
关键词
D O I
10.1063/1.1658224
中图分类号
O59 [应用物理学];
学科分类号
摘要
In this paper, the surface charge formation characteristics of thermoelectrets, prepared at different polarizing fields from a plant product, Boswellia Glabra, have been presented. A comparatively easy method for the fabrication of thermoelectrets of this meterial has been developed. The results obtained show that this plant product is a suitable material for electret preparation. Both the anode and cathode sides show the same sign of charge, without showing any charge reversal up to a polarizing field of 1000 V per mm thickness of the sample. The sample, prepared at zero field, indicates that the charge obtained with low-field samples is not due to the molding charge. The results also fail to find experimental conformation of Gross's and Gemant's hypothesis concerning the production of homocharge with regard to the cathode sides of the low-field Boswellia Glabra electrets. © 1969 The American Institute of Physics.
引用
收藏
页码:3487 / &
相关论文
共 17 条
  • [1] On the permanent electret
    Eguchi, M
    [J]. PHILOSOPHICAL MAGAZINE, 1925, 49 (289): : 178 - 192
  • [2] FILIPPOVA KV, 1958, IZV AN SSSR FIZ, V22, P343
  • [3] FROIMAN AI, 1956, KRISTALLOGRAFIYA, V1, P342
  • [4] Gemant A, 1935, PHILOS MAG, V20, P929
  • [5] GEMANT A, 1953, DIRECT CURRENT
  • [6] GEMANT A, 1935, PHIL MAG, V20, P136
  • [7] Gross B., 1964, CHARGE STORAGE SOLID
  • [8] CHARACTERISTICS OF PLASTIC ELECTRETS
    JAIN, VK
    PILLAI, PKC
    [J]. PHYSICA STATUS SOLIDI, 1968, 28 (01): : 415 - &
  • [9] The permanent polarisation of solid dielectrics
    Mikola, S
    [J]. ZEITSCHRIFT FUR PHYSIK, 1925, 32 : 476 - 488
  • [10] NADZHAKOV G, 1936, GODISHNIK FIZ MAT SO, V33, P409