HOT ISOSTATIC PRESSING AND CHARACTERIZATION OF SOL-GEL-DERIVED CHROMIUM(III) OXIDE

被引：52
作者：
KAWABATA, A
YOSHINAKA, M
HIROTA, K
YAMAGUCHI, O
机构：
[1] Department of Molecular Science and Technology, Faculty of Engineering, Doshisha University, Tanabe, Kyoto
来源：
JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1995年 / 78卷 / 08期
关键词：
D O I：
10.1111/j.1151-2916.1995.tb08655.x
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Chromium(III) oxide (Cr2O3) crystallizes at low temperatures from an amorphous material prepared by adding hydrazine monohydrate to an aqueous solution of Cr(NO3)(3). 9H(2)O. Individual particles of Cr2O3 tend toward a hexago nal morphology above 800 degrees C. Well-densified Cr2O3 pellets (98.8% of theoretical density) have been fabricated by hot isostatic pressing for 2 h at 1100 degrees C and 196 MPa. Their fracture toughness is 4.4 MPa . m(1/2). The sample annealed in air for 12 h at 1300 degrees C exhibits a high electrical conductivity of 3.6 Ohm-1.m(-1) at 700 degrees C.
引用
收藏
页码：2271 / 2273
页数：3
相关论文
共 11 条
  • [1] Adler D., 1970, Radiation Effects, P123, DOI 10.1080/00337577008234978
  • [2] SINTERING CHROMIUM-OXIDE WITH THE AID OF TIO2
    CALLISTER, WD
    JOHNSON, ML
    CUTLER, IB
    URE, RW
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1979, 62 (3-4) : 208 - 211
  • [3] EVANS AG, 1984, J AM CERAM SOC, V67, P255, DOI 10.1111/j.1151-2916.1984.tb18842.x
  • [4] KODERA K, 1962, POWDERS THEORY APPL, P132
  • [5] LACKEY WJ, 1987, ADV CERAM MATER, V2, P24
  • [6] EFFECT OF TIO2 ON THE SINTERING AND THE ELECTRICAL-CONDUCTIVITY OF CR2O3
    NAGAI, H
    OHBAYASHI, K
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1989, 72 (03) : 400 - 403
  • [7] EVALUATION OF KLC OF BRITTLE SOLIDS BY THE INDENTATION METHOD WITH LOW CRACK-TO-INDENT RATIOS
    NIIHARA, K
    MORENA, R
    HASSELMAN, DPH
    [J]. JOURNAL OF MATERIALS SCIENCE LETTERS, 1982, 1 (01) : 13 - 16
  • [8] FINAL SINTERING OF CR2O3
    OWNBY, PD
    JUNGQUIS.GE
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1972, 55 (09) : 433 - &
  • [9] CATION TRACER DIFFUSION IN CR2O3 AND CR2O3-0.09 WT-PERCENT Y2O3
    PARK, JH
    KING, WE
    ROTHMAN, SJ
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1987, 70 (12) : 880 - 885
  • [10] YAMAGUCHI A, 1980, YOGYO KYOKAISHI, V88, P32
12