EFFECT OF FE CONTENT ON THE MECHANICAL ALLOYING AND MECHANICAL-PROPERTIES OF AL-FE ALLOYS

被引:18
作者
NIU, XP [1 ]
FROYEN, L [1 ]
DELAEY, L [1 ]
PEYTOUR, C [1 ]
机构
[1] DIRECT ETUDES MAT,F-92109 BOULOGNE,FRANCE
关键词
D O I
10.1007/BF00357340
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Al-Fe alloys with Fe contents ranging from 5 to 12 wt% are produced by a double mechanical alloying process (DMA) which consists of a first step of mechanical alloying (MA1) applied to elemental Al and Fe powders, with subsequent heat treatment of MA1 powders to promote the formation of Al-Fe intermetallic phases, and a second mechanical alloying step (MA2) to refine the intermetallic phase, and consolidation of the produced powders by combination of degassing and hot extrusion. The effect of Fe content on the process, as well as on the mechanical properties of the extruded alloys, has been extensively studied. The alloys produced by this process show excellent tensile strength and stiffness at room and elevated temperatures due to the strengthening of Al by intermetallics, as well as to the stabilization of the structure by inert dispersoids.
引用
收藏
页码:3724 / 3732
页数:9
相关论文
共 25 条
[21]   ELASTIC-MODULUS VERSUS MELTING TEMPERATURE IN ALUMINUM BASED INTERMETALLICS [J].
SKINNER, DJ ;
ZEDALIS, M .
SCRIPTA METALLURGICA, 1988, 22 (11) :1783-1785
[22]   INTERMETALLIC PHASES FORMED DURING DC-CASTING OF AN AL-0.25 WT PCT FE-0.13 WT PCT SI ALLOY [J].
SKJERPE, P .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (02) :189-200
[23]   MECHANICAL-PROPERTIES OF AL-8WT PERCENT FE-BASED ALLOYS PREPARED BY RAPID QUENCHING FROM LIQUID-STATE [J].
THURSFIELD, G ;
STOWELL, MJ .
JOURNAL OF MATERIALS SCIENCE, 1974, 9 (10) :1644-1660
[24]  
ZAIDI MA, 1985, MATER SCI TECH SER, V1, P737, DOI 10.1179/026708385790124288
[25]  
1991, POWDER DIFFRACTION F