USE OF SUBSIZED SPECIMEN FOR EVALUATING THE STRENGTH AND FRACTURE-TOUGHNESS OF IRRADIATED 2 1/4 CR-1 M0 STEEL

被引：4

作者：

MAO, X

TAKAHASHI, H

KODAIRA, T

机构：

[1] Department of Mechanical Engineering, University of Calgary, Calgary, AB

[2] Research Institute for Fracture Technology, Tohoku University, Sendai

来源：

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME | 1992年 / 114卷 / 02期

关键词：

D O I：

10.1115/1.2904157

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The procedure of the determination of yield and ultimate strengths of irradiated 2 1/4 Cr-1 M0 steel using small punch specimen (10 mm by 10 mm by 0.5 mm) has been demonstrated. The result was compared with the result obtained from conventional tensile test. Fracture toughness of irradiated 2 1/4 Cr-1 M0 steel was measured by use of subsized CT specimen and D.C. electrical potential method. Owing to irradiation hardening of 2 1/4 Cr-1 M0 steel, yield and ultimate strength increase substantially and fracture toughness decreases 37 percent when the steel is irradiated to a fluence of 3.2 x 10(23) n/m2. The small punch and subsized CT specimen can be used for irradiation test so that considerable irradiation space will be saved.

引用

页码：168 / 171

页数：4

共 50 条

[1] FRACTURE-TOUGHNESS BEHAVIOR OF UNIRRADIATED AND IRRADIATED 2-1/4 CR-1 MO STEEL PLATE AND WELDMENT
MILLS, WJ
NUCLEAR TECHNOLOGY, 1984, 64 (02) : 175 - 185
[2] PLANE-STRAIN FRACTURE-TOUGHNESS OF A 1/2-PERCENT CR-1/2-PERCENT MO-1/4-PERCENT V CAST STEEL
BALOGUM, SA
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1979, 32 (05): : 374 - 378
[3] Fracture toughness of irradiated modified 9Cr-1Mo steel
Kim, Sung Ho
Yoon, Ji-Hyun
Ryu, Woo Seog
Lee, Chan Bock
Hong, Jun Hwa
JOURNAL OF NUCLEAR MATERIALS, 2009, 386-88 : 387 - 389
[4] CREEP-RUPTURE STRENGTH OF ANNEALED 2-1/4 CR-1 MO STEEL
KLUEH, RL
SCRIPTA METALLURGICA, 1985, 19 (07): : 789 - 793
[5] DECARBURIZATION BEHAVIOR OF 2 1/4 CR-1 MO FERRITIC STEEL
SHIELS, SA
BAGNALL, C
ORBON, S
TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1974, 18 (JUN23): : 115 - 116
[6] CREEP OF DECARBURIZED AND AGED 2-1/4 CR-1 MO STEEL
KLUEH, RL
JOURNAL OF NUCLEAR MATERIALS, 1981, 96 (1-2) : 187 - 195
[7] ANALYSIS OF DECARBURIZATION AND AGING PROCESSES IN 2 1/4 CR-1 MO STEEL
KLUEH, RL
LEITNAKER, JM
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (11): : 2089 - 2093
[8] AN ANALYSIS OF TERTIARY CREEP IN 2(1/4) CR-1 MO-STEEL
GHOSH, RN
SINGH, R
KUMAR, R
SCRIPTA METALLURGICA, 1985, 19 (07): : 801 - 804
[9] ELEVATED-TEMPERATURE TENSILE PROPERTIES OF IRRADIATED 21/4 CR-1 MO STEEL
KLUEH, RL
VITEK, JM
JOURNAL OF NUCLEAR MATERIALS, 1984, 126 (01) : 9 - 17
[10] COMPOSITION OF ETA CARBIDE PHASE IN 2 1/4 CR-1 MO STEEL
LEITNAKER, JM
KLUEH, RL
LAING, WR
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (10): : 1949 - 1955

← 1 2 3 4 5 →