AGING DUE TO GAMMA-RADIATION OF A CROSS-LINKED POLYETHYLENE

被引:9
作者
SPADARO, G [1 ]
CALDERARO, E [1 ]
RIZZO, G [1 ]
机构
[1] UNIV PALERMO,DIPARTIMENTO INGN NUCL,I-90134 PALERMO,ITALY
关键词
D O I
10.1016/0014-3057(92)90185-5
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Ageing due to gamma radiation in air of a low density polyethylene, previously crosslinked by gamma-radiation under vacuum, is studied. The aim is to try to separate crosslinking and degradation phenomena which usually occur during irradiation in air. The effect of irradiation is investigated by means of solubility and swelling and calorimetric measurements, and stress-strain tensile tests. Gamma-radiation in air of the crosslinked polymer causes mainly oxidative degradation, the extent of which depends on irradiation dose rate.
引用
收藏
页码:257 / 259
页数:3
相关论文
共 9 条
[1]  
CALDERARO E, 1980, QUADERNI I APPLICAZI, V3
[2]   HETEROGENEOUS OXIDATIVE-DEGRADATION IN IRRADIATED POLYMERS [J].
CLOUGH, RL ;
GILLEN, KT ;
QUINTANA, CA .
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 1985, 23 (02) :359-377
[3]  
JENKINS H, 1983, SCI PHYS B, V11, P155
[4]  
RIZZO G, 1990, MATER ENG, V1, P585
[5]   RADIATION-INDUCED OXIDATIVE-DEGRADATION OF POLYMERS .4. DOSE-RATE EFFECTS ON CHEMICAL AND MECHANICAL-PROPERTIES [J].
SEGUCHI, T ;
ARAKAWA, K ;
HAYAKAWA, N ;
MACHI, S .
RADIATION PHYSICS AND CHEMISTRY, 1981, 18 (3-4) :671-678
[6]   RADIATION-INDUCED OXIDATIVE-DEGRADATION OF POLYMERS .2. EFFECTS OF RADIATION ON SWELLING AND GEL FRACTION OF POLYMERS [J].
SEGUCHI, T ;
ARAKAWA, K ;
HAYAKAWA, N ;
WATANABE, Y ;
KURIYAMA, I .
RADIATION PHYSICS AND CHEMISTRY, 1982, 19 (04) :321-327
[7]   RADIATION-INDUCED DEGRADATION AND CROSSLINKING OF LOW-DENSITY POLYETHYLENE - EFFECT OF DOSE-RATE AND INTEGRATED DOSE [J].
SPADARO, G ;
CALDERARO, E ;
RIZZO, G .
ACTA POLYMERICA, 1989, 40 (11) :702-705
[8]  
STRUIK LCE, 1978, PHYSICAL AGING AMORP
[9]  
1979, 5443 BUR CENTR COMM