DIFFUSION OF CADMIUM IN LEAD

The diffusivity D2 of cadmium in high-purity lead single crystals has been measured from 150 °C to the melting point, using tracer and sectioning techniques, and is described by D2=0.409 exp(-21 230RT) cm2/sec. Lead self-diffusivity is enhanced by the addition of cadmium in accordance with D1=D10×(1+b1X+b2X2+b3X3), where bi are the linear and higher-order enhancement factors, and D10 and D1 are the self-diffusivity of lead in pure lead and in lead alloys containing X atom fraction of cadmium, respectively. It is found that b1≅D2D10, varying from 19 to 45 over the temperature range 300-198 °C. It is shown from the results of Howard and Manning that the minimum linear enhancement factor for the vacancy mechanism is bmin=-18+1.9448(D2D10), substantially larger than that observed. The fast diffusion of cadmium cannot then be accounted for on the basis of the model proposed by Lidiard for the simple vacancy mechanism. It is suggested that cadmium, like the solutes Ag, Au, and Cu, dissolves both interstitially and substitutionally in lead, the enhancement of lead self-diffusion being associated with an interaction between vacancies and interstitial cadmium ions. A comparison of diffusion data for several impurities in lead shows that the dominant mechanism of solute diffusion is determined primarily by solute valence. Since the dominant diffusion mechanism of a solute is a natural consequence of its degree of interstitial dissolution, it is proposed that solute valence plays a major role in determining the energetics of interstitial dissolution. © 1969 The American Physical Society.