SUPERCONDUCTING GLASS IN THE SYSTEM NA2O-ZRO2-SIO2-P2O5

被引：4
作者：
HOJ, JW
ENGELL, J
机构：
[1] Institute for Mineral Industry, The Technical University of Denmark, DK-2800 Lyngby
来源：
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY | 1992年 / 14卷 / 02期
关键词：
D O I：
10.1016/0921-5107(92)90122-P
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The conductivity, transition temperatures and thermal expansion coefficients are given for a series of glasses in the proximity of the Nasicon solid solution. The lowest resistivity found was 303 OMEGA cm at 300-degrees-C and E(a) = 0.53 eV. The transition temperatures range from 705 to 823-degrees-C.
引用
收藏
页码：231 / 234
页数：4
相关论文
共 8 条
[1]   NASICON - AMORPHOUS TO CRYSTALLINE COMPOUNDS [J].
BOILOT, JP ;
COLOMBAN, P ;
COLLIN, G .
SOLID STATE IONICS, 1986, 18-9 (pt 2) :974-980
[2]   FORMATION OF SUPERIONIC GELS AND GLASSES BY LOW-TEMPERATURE CHEMICAL POLYMERIZATION [J].
BOILOT, JP ;
COLOMBAN, P ;
BLANCHARD, N .
SOLID STATE IONICS, 1983, 9-10 (DEC) :639-643
[3]   FABRICATION OF NASICON ELECTROLYTES FROM METAL ALKOXIDE DERIVED GELS [J].
ENGELL, J ;
MORTENSEN, S ;
MOLLER, L .
SOLID STATE IONICS, 1983, 9-10 (DEC) :877-884
[4]  
HOJ JW, 1989, MATERIALIS RES SOC S, V135, P301
[5]  
HOJ JW, 1988, THESIS TU DENMARK
[6]   NA+-ION CONDUCTING GLASSES [J].
HUNTER, CC ;
INGRAM, MD .
SOLID STATE IONICS, 1984, 14 (01) :31-40
[7]   NASIGLAS - A NEW VITREOUS ELECTROLYTE [J].
SUSMAN, S ;
DELBECQ, CJ ;
MCMILLAN, JA ;
ROCHE, MF .
SOLID STATE IONICS, 1983, 9-10 (DEC) :667-673
[8]   PROPERTIES OF NASICON ELECTROLYTES PREPARED FROM ALKOXIDE DERIVED GELS - IONIC-CONDUCTIVITY, DURABILITY IN MOLTEN SODIUM AND STRENGTH TEST DATA [J].
YDEANDERSEN, S ;
LUNDSGAARD, JS ;
MOLLER, L ;
ENGELL, J .
SOLID STATE IONICS, 1984, 14 (01) :73-79
1