SULFIDE CAPACITIES OF CAO-AL2O3-MGO AND CAO-AL2O3-SIO2 SLAGS

被引：52

作者：

HINO, M ^{[1
]}

KITAGAWA, S ^{[1
]}

BANYA, S ^{[1
]}

机构：

[1] TOHOKU UNIV,GRAD SCH,SENDAI,MIYAGI 980,JAPAN

来源：

ISIJ INTERNATIONAL | 1993年 / 33卷 / 01期

关键词：

SULFIDE CAPACITY; SULFUR DISTRIBUTION RATIO; SECONDARY STEELMAKING; SLAG; PHYSICAL CHEMISTRY;

D O I：

10.2355/isijinternational.33.36

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The sulphide capacities of CaO-Al2O3, CaO-Al2O3-MgO and CaO-Al2O3-SiO2 slags were studied at 1 823 to 1 923 K to estimate the sulphur distribution ratio between secondary steelmaking slag and liquid steel. From the obtained results, it was confirmed that substitution of MgO or SiO2 for CaO at a given N(Al2O3) decreased the sulphide capacities in both systems of CaO-Al2O3-MgO and CaO-Al2O3-SiO2. The evaluated maximum values of sulphur distribution ratio for both slags were higher than 1 000 at 1 873 K on the condition of CaO-saturation if the dissolved aluminium content in steel was assumed to be 0.01 mass%.

引用

页码：36 / 42

页数：7

共 23 条

[11]

Kalyanram M., 1961, BRIT CERAM T, V60, P135

[12]

Kalyanram M.R., 1960, J IRON STEEL I, V195, P58

[13] ACTIVITIES OF SILICA IN THE LIME+ALUMINA+SILICA SYSTEM [J].

KAY, DAR ;

TAYLOR, J .

TRANSACTIONS OF THE FARADAY SOCIETY, 1960, 56 (09) :1372-1386

[14]

KOR GJW, 1968, J IRON STEEL I, V206, P700

[15]

NAGABAYASHI R, 1988, TETSU TO HAGANE, V74, P1770

[16] DISTRIBUTION OF SULFUR BETWEEN LIQUID-IRON AND FETO-(CAO+MGO)-(SIO2+P2O5) PHOSPHATE SLAGS [J].

NAGABAYASHI, R ;

HINO, M ;

BANYA, S .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1990, 76 (02) :183-190

[17] MATHEMATICAL EXPRESSION OF PHOSPHORUS DISTRIBUTION IN STEELMAKING PROCESS BY QUADRATIC FORMALISM [J].

NAGABAYASHI, R ;

HINO, M ;

BANYA, S .

ISIJ INTERNATIONAL, 1989, 29 (02) :140-147

[18]

NAGABAYASHI R, 1988, TETSU TO HAGANE, V74, P1585

[19] EQUILIBRIUM-S DISTRIBUTION BETWEEN MOLTEN CALCIUM ALUMINATE AND STEEL .1. CAS-CAO-AL2O3 MELTS EQUILIBRATED WITH LIQUID FE CONTAINING AL AND S [J].

OZTURK, B ;

TURKDOGAN, ET .

METAL SCIENCE, 1984, 18 (06) :299-305

[20]

REIN RH, 1965, T METALL SOC AIME, V233, P415

← 1 2 3 →