SPIN ORIENTATION IN FE AND FE-CO THIN-FILMS

被引：13
作者：
DINHUT, JF
EYMERY, JP
机构：
[1] Laboratoire de Métallurgie Physique, URA 131 du CNRS, 86022 Poitiers, 40, avenue du Recteur Pineau
来源：
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS | 1991年 / 93卷
关键词：
D O I：
10.1016/0304-8853(91)90340-G
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Evaporated iron and iron-cobalt thin films in the range 20-1500 nm were deposited on various rotating substrates in UHV conditions (2 x 10(-7) Pa). Spin orientation, deduced from Mossbauer spectra, rotates from in plane to out of plane (nearly perpendicular) position when thickness increases. This behaviour is related to the columnar structure observed by TEM and explained by the enhanced surface diffusion in the low residual pressure. The stability of the perpendicular spin orientation is also investigated by subsequent annealing up to 700-degrees-C.
引用
收藏
页码：252 / 256
页数：5
相关论文
共 8 条
[1]   COLUMNAR MICROSTRUCTURE IN VAPOR-DEPOSITED THIN-FILMS [J].
DIRKS, AG ;
LEAMY, HJ .
THIN SOLID FILMS, 1977, 47 (03) :219-233
[2]   COLUMNAR GROWTH IN EVAPORATED IRON FILMS [J].
FUJIWARA, H ;
HARA, K ;
KAMIYA, M ;
HASHIMOTO, T ;
OKAMOTO, K .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1983, 35 (1-3) :296-298
[3]   OBLIQUE-INCIDENCE ANISOTROPY OF THE IRON FILMS EVAPORATED AT LOW SUBSTRATE TEMPERATURES [J].
HARA, K ;
KAMIYA, M ;
HASHIMOTO, T ;
OKAMOTO, K ;
FUJIWARA, H .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1988, 73 (02) :161-166
[4]   COLUMNAR STRUCTURE AND TEXTURE OF IRON FILMS EVAPORATED AT OBLIQUE-INCIDENCE [J].
HASHIMOTO, T ;
OKAMOTO, K ;
HARA, K ;
KAMIYA, M ;
FUJIWARA, H .
THIN SOLID FILMS, 1982, 91 (02) :145-154
[5]   GRAIN-STRUCTURE AND MAGNETIC-ANISOTROPY OF FE FILM EVAPORATED OBLIQUELY FROM 2 SOURCES [J].
KEITOKU, S ;
NISHIOKA, K .
JAPANESE JOURNAL OF APPLIED PHYSICS, 1981, 20 (07) :1249-1253
[6]   COLUMNAR STRUCTURE AND TEXTURE OF IRON FILMS PREPARED AT VARIOUS EVAPORATION RATES [J].
OKAMOTO, K ;
HASHIMOTO, T ;
HARA, K ;
KAMIYA, M ;
FUJIWARA, H .
THIN SOLID FILMS, 1987, 147 (03) :299-311
[7]  
OSAWA K, 1984, J MAGN MAGN MATER, V46, P123
[8]   FABRICATION AND PROPERTIES OF FE-FE OXIDE AND CO-CO OXIDE-FILMS [J].
SCHNEIDER, JW ;
STOFFEL, AM ;
TRIPPEL, G .
IEEE TRANSACTIONS ON MAGNETICS, 1973, MAG9 (03) :183-185
1