J-RESISTANCE CURVE AND DUCTILE TEARING OF A MILD-STEEL

The onset of ductile tearing at room temperature of mild steel BS 15 was studied using side grooved compact tension specimens. The approach to this problem was divided conveniently into two basic parts: first, identification and evaluation of the toughness at initiation of crack extension, and second, assessment and characterization of the subsequent crack growth behaviour. The critical value of the J integral for crack initiation, Jc was obtained using two different techniques: the multispecimen method and a single specimen compliance test. It was found that the latter could be used with much larger unloading than originally proposed. This has the advantage of greater accuracy in the determination of the compliance, and consequently in the evaluation of crack extension. In the second part of the work, resistance curves were obtained applying two different approaches. The resistance curves obtained following the more exact method were used for the determination of the tearing modulus T of the material, and the values thus derived, compared with a selection of other steels. © 1979.