SUBCRITICAL SURFACE CRACK-GROWTH IN BOROSILICATE GLASS UNDER THERMAL FATIGUE

被引：5
作者：
FETT, T [1 ]
KELLER, K [1 ]
MUNZ, D [1 ]
KUBLER, J [1 ]
机构：
[1] EIDGENOSS MAT PRUFUNGS & FORSCH ANSTALT, DUBENDORF, SWITZERLAND
来源：
THEORETICAL AND APPLIED FRACTURE MECHANICS | 1991年 / 16卷 / 01期
关键词：
D O I：
10.1016/0167-8442(91)90038-L
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The thermal fatigue behaviour of glass is studied analytically and experimentally. Temperatures and stress intensity factors were calculated for cylindrical test specimens containing semi-elliptical surface cracks. The calculations of crack propagation during the fatigue tests were performed on the assumption that only subcritical crack growth as occurring in static tests is responsible for crack propagation and no additional cyclic damage occurs. The predictions of failure are in rather good agreement with the experiments.
引用
收藏
页码：27 / 34
页数：8
相关论文
共 50 条
  • [21] SUBCRITICAL CRACK-GROWTH - FATIGUE, CREEP AND STRESS-CORROSION CRACKING
    TOMKINS, B
    [J]. PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1981, 299 (1446): : 31 - 44
  • [22] FATIGUE CRACK-GROWTH UNDER CONTINUOUS RADIATION
    WEERTMAN, J
    GREEN, WV
    [J]. JOURNAL OF NUCLEAR MATERIALS, 1981, 97 (03) : 254 - 258
  • [23] FATIGUE CRACK-GROWTH IN LIQUIDS UNDER PRESSURE
    PLUMBRIDGE, WJ
    ROSS, PJ
    PARRY, JSC
    [J]. MATERIALS SCIENCE AND ENGINEERING, 1985, 68 (02): : 219 - 232
  • [24] FATIGUE CRACK-GROWTH UNDER RANDOM LOADING
    ALAWI, H
    SHABAN, M
    [J]. ENGINEERING FRACTURE MECHANICS, 1989, 32 (05) : 845 - 854
  • [25] FATIGUE CRACK-GROWTH UNDER COMPRESSIVE LOADING
    FLECK, NA
    SHIN, CS
    SMITH, RA
    [J]. ENGINEERING FRACTURE MECHANICS, 1985, 21 (01) : 173 - +
  • [26] FATIGUE CRACK-GROWTH UNDER BIAXIAL LOADING
    LAM, YC
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1993, 16 (04) : 429 - 440
  • [27] ON FATIGUE CRACK-GROWTH UNDER RANDOM LOADING
    ZHU, WQ
    LIN, YK
    LEI, Y
    [J]. ENGINEERING FRACTURE MECHANICS, 1992, 43 (01) : 1 - 12
  • [28] FATIGUE CRACK-GROWTH
    BATES, RC
    [J]. JOURNAL OF METALS, 1983, 35 (12): : 73 - 73
  • [29] SUBCRITICAL CRACK-GROWTH MECHANISMS IN CERAMICS
    WIEDERHORN, SM
    [J]. JOURNAL OF METALS, 1981, 33 (09): : A11 - A11
  • [30] SUBCRITICAL CRACK-GROWTH IN FERROELECTRIC CERAMICS
    CHUSHKO, VM
    [J]. STRENGTH OF MATERIALS, 1981, 13 (07) : 864 - 868
12345