The effect of the test machine on the failure mode in lubricated rolling contact of silicon nitride

被引：35
作者：
Hadfield, M
Stolarski, TA
机构：
[1] Brunel University, Department of Mechanical Engineering, Uxbridge
来源：
TRIBOLOGY INTERNATIONAL | 1995年 / 28卷 / 06期
关键词：
ceramics; rolling contact; fatigue;
D O I：
10.1016/0301-679X(95)00022-V
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The experimentally assessed performance of technical ceramics in lubricated rolling contact is presented. Special emphasis is on the failure modes resulting from the test conditions encountered in the model rolling contact used.
引用
收藏
页码：377 / 382
页数：6
相关论文
共 21 条
  • [1] Transient wear of silicon nitride in lubricated rolling contact
    Chao, LY
    Lakshminarayanan, R
    Iyer, N
    Lin, GY
    Shetty, DK
    WEAR, 1998, 223 (1-2) : 58 - 65
  • [2] The influence of test lubricants on the rolling contact fatigue failure mechanisms of silicon nitride ceramic
    Zhao, P
    Hadfield, M
    Wang, Y
    Vieillard, C
    WEAR, 2004, 257 (9-10) : 1047 - 1057
  • [3] The influence of heterogeneous porosity on silicon nitride/steel wear in lubricated rolling contact
    Kang, J
    Hadfield, M
    CERAMICS INTERNATIONAL, 2000, 26 (03) : 315 - 324
  • [4] Rolling contact induced failures of silicon nitride
    Stolarski, T. A.
    Tobe, S.
    TRIBOLOGY LETTERS, 1997, 3 (04) : 349 - 357
  • [5] The effects of material combination and surface roughness in lubricated silicon nitride/steel rolling contact fatigue
    Kang, J
    Hadfield, M
    Ahmed, R
    MATERIALS & DESIGN, 2003, 24 (01) : 1 - 13
  • [6] Flaking Failure in Silicon Nitride under Reciprocating Rolling Contact Fatigue
    Kida, Katsuyuki
    HIGH PERFORMANCE STRUCTURES AND MATERIALS ENGINEERING, PTS 1 AND 2, 2011, 217-218 : 866 - 873
  • [7] Roughness Effect in Micropitting and Rolling Contact Fatigue of Silicon Nitride
    Mosleh, Mohsen
    Bradshaw, Keron K.
    Smith, Sonya T.
    Belk, John H.
    Shirvani, Khosro A.
    CERAMICS-SWITZERLAND, 2019, 2 (01): : 135 - 147
  • [8] Residual stress variations during rolling contact fatigue of refrigerant lubricated silicon nitride bearing elements
    Khan, Zulfiqar Ahmad
    Hadfield, Mark
    Tobe, Shogo
    Wang, Ying
    CERAMICS INTERNATIONAL, 2006, 32 (07) : 751 - 754
  • [9] Damage initiation and evolution in silicon nitride under non-conforming lubricated hybrid rolling contact
    Raga, Rahul
    Khader, Lyas
    Chlup, Zdenek
    Kailer, Andreas
    WEAR, 2016, 360 : 147 - 159
  • [10] Wear of steel in rolling contact with silicon nitride
    Lakshminarayanan, R
    Chao, LY
    Iyer, N
    Shetty, DK
    WEAR, 1997, 210 (1-2) : 278 - 286
123