EFFECT OF SURFACE TREATMENTS ON THE REPAIR STRENGTH OF A LIGHT-ACTIVATED DENTURE REPAIR RESIN USING CENSORED-DATA

被引:15
作者
OLVERA, N
DERIJK, WG
机构
[1] UNIV ILLINOIS,COLL DENT,CHICAGO,IL 60612
[2] UNIV TEXAS,DENT BRANCH,DEPT CONTINUING EDUC,HOUSTON,TX
[3] UNIV TEXAS,HLTH SCI CTR,SCH DENT,SAN ANTONIO,TX 78284
关键词
D O I
10.1016/0109-5641(94)90052-3
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
Objectives. The aim of this study was to evaluate the effect of three different chemical surface modifications on the bond strength of light-activated denture repair resin (Triad, Dentsply International) to a heat-cured resin (Lucitone, Dentsply international). Methods. Transverse flexure test specimens were made, with surface treatment of 1) Triad bonding agent, 2) unreacted Lucitone monomer, and 3) a 1:1 mixture of methylene chloride and monomer, using two different application times (2 and 4 min). For all except one group, 18 specimens were made. The controls were solid single composition bars, 18 for each material. The elastic modulus in transverse flexure was measured for each material. The statistical analysis employed the Weibull distribution. Fracture strength values were obtained in a three-point flexure test. Results. It was noted that many fractures occurred away from the interface and the center member of the test fixture. For those fractures, the observed fracture strength is a censored value of the fracture strength. Algorithms for the statistical treatment of censored data were used to get the maximum likelihood estimates of the fracture strength. A mechanical model showed that under three-point bending of a beam of two joined materials, fractures will occur in the part with the higher elastic modulus. This finding is indeed observed in the data. The 4 min monomer treatment showed the highest estimate of the bond strength (187.8 MPa). Significance. Censored data can be used to obtain fracture strength estimates, and the censoring indicates that the bond strength may exceed the strength of the bulk material.
引用
收藏
页码:122 / 127
页数:6
相关论文
共 17 条
[1]   REPAIR OF FRACTURED ACRYLIC RESIN [J].
BEYLI, MS ;
VONFRAUNHOFER, JA .
JOURNAL OF PROSTHETIC DENTISTRY, 1980, 44 (05) :497-503
[3]  
DERIJK WG, 1988, 3RD P WORLD BIOM C K, P251
[4]  
DERIJK WG, 1988, P ACS DIVISION POLYM, V59, P141
[5]   BOND STRENGTHS OF CHEMICALLY DISSIMILAR REPAIRED COMPOSITE RESINS [J].
GREGORY, WA ;
POUNDER, B ;
BAKUS, E .
JOURNAL OF PROSTHETIC DENTISTRY, 1990, 64 (06) :664-668
[6]   EFFECT OF JOINT SURFACE CONTOURS ON TRANSVERSE STRENGTH OF REPAIRED ACRYLIC RESIN [J].
HARRISON, WM ;
STANSBURY, BE .
JOURNAL OF PROSTHETIC DENTISTRY, 1970, 23 (04) :464-+
[7]  
LAWLESS JF, 1982, STAT MODELS METHODS, P141
[8]  
MANN NR, 1974, METHODS STATISTICAL, P220
[9]  
NASH NA, 1972, THEORY PROBLEMS STRE, P129
[10]  
NASH NA, 1972, THEORY PROBLEMS STRE, P162