INFLUENCE OF ISOTHERMAL SOLIDIFICATION ON MICROSTRUCTURAL DEVELOPMENT IN NI-SI-B FILLER METALS

被引：32
作者：
GALE, WF
WALLACH, ER
机构：
[1] Department of Materials Science and Metallurgy, University of Cambridge, Cambridge
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 1991年 / 7卷 / 12期
关键词：
D O I：
10.1179/mst.1991.7.12.1143
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An examination is reported of the microstructure of joints between nickel substrates fabricated using Ni-Si-B filler metal (AWS classification BNi-3). This investigation was undertaken because the presence of residual boride and silicide phases after joining can affect the subsequent mechanical properties of the joint. The microstructures developed in the joints are compared with those formed in similarly heat treated filler metal. Various models of the transient liquid phase process are also considered and predicted times to complete isothermal solidification are compared with experimental values. An initial examination of the influence on filler metal microstructure of a ternary addition (chromium) to the substrate is included.
引用
收藏
页码：1143 / 1148
页数：6
相关论文
共 17 条
[1]  
BARBASSAT MH, 1986, HIGH TEMPERATURE ALL, P897
[2]  
Crank J., 1975, MATH DIFFUSION, VSecond, P414, DOI 10.1016/0306-4549(77)90072-X
[3]  
DUVALL DS, 1974, WELD J, V53, P203
[4]   MICROSTRUCTURAL DEVELOPMENT IN TRANSIENT LIQUID-PHASE BONDING [J].
GALE, WF ;
WALLACH, ER .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (10) :2451-2457
[5]  
GALE WF, 1990, RECENT TRENDS IN WELDING SCIENCE AND TECHNOLOGY, TWR 89, P529
[6]   WETTING OF NICKEL-ALLOYS BY NICKEL BASED BRAZES [J].
GALE, WF ;
WALLACH, ER .
MATERIALS SCIENCE AND TECHNOLOGY, 1990, 6 (02) :170-175
[7]  
JOHNSON R, 1981, WELD J, V60, pS185
[8]  
KUCERA J, 1984, KOVOVE MATER, V22, P250
[9]   TERNARY-SYSTEM NICKEL-BORON-SILICON [J].
LUGSCHEIDER, E ;
REIMANN, H ;
KNOTEK, O .
MONATSHEFTE FUR CHEMIE, 1975, 106 (05) :1155-1165
[10]  
Massalski T.B., 1986, BINARY ALLOY PHASE D, P366
12