ULTRAHIGH NUCLEATION DENSITY FOR GROWTH OF SMOOTH DIAMOND FILMS

被引：36
|
作者：
YANG, GS
ASLAM, M
机构：
[1] Department of Electrical Engineering, Michigan State University, East Lansing
来源：
APPLIED PHYSICS LETTERS | 1995年 / 66卷 / 03期
关键词：
D O I：
10.1063/1.113528
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
An ultrahigh density seeding process of diamond thin-film deposition is demonstrated. Diamond powders with average grain sizes of 0.038 and 0.101 μm were used to study the surface roughness as a function of deposition time, film thickness, and nucleation density. The diamond films, prepared by hot filament chemical vapor deposition, were characterized by atomic force microscopy, scanning electron microscopy, and Raman spectroscopy. An extremely high nucleation density on the order of 1011 cm-2 was achieved by coating 0.038 μm diamond powder on the surface of the Si substrate. One micron thick films were obtained with the mean surface roughness of 30 nm. © 1995 American Institute of Physics.
引用
收藏
页码：311 / 313
页数：3
相关论文
共 50 条
  • [21] EFFECT OF NUCLEATION DENSITY ON THE MORPHOLOGY OF DIAMOND THIN-FILMS
    PARK, YS
    KIM, SH
    LEE, JW
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS BRIEF COMMUNICATIONS & REVIEW PAPERS, 1994, 33 (11): : 6320 - 6324
  • [22] Synthesis and characterization of smooth ultrananocrystalline diamond films via low pressure bias-enhanced nucleation and growth
    Chen, Y. C.
    Zhong, X. Y.
    Konicek, A. R.
    Grierson, D. S.
    Tai, N. H.
    Lin, I. N.
    Kabius, B.
    Hiller, J. M.
    Sumant, A. V.
    Carpick, R. W.
    Auciello, O.
    APPLIED PHYSICS LETTERS, 2008, 92 (13)
  • [23] The influence of nitrogen and oxygen on the high nucleation density diamond growth
    Gan, Zhiwen
    Gan, Zhiyin
    Zhang, Dongliang
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 122
  • [24] EFFECT OF OXYGEN ON THE NUCLEATION AND GROWTH OF DIAMOND THIN-FILMS
    SHAH, SI
    WAITE, MM
    APPLIED PHYSICS LETTERS, 1992, 61 (26) : 3113 - 3115
  • [25] ROLE OF THE NUCLEATION STEP IN THE GROWTH-RATE OF DIAMOND FILMS
    FAYETTE, L
    MERMOUX, M
    MARCUS, B
    DIAMOND AND RELATED MATERIALS, 1994, 3 (4-6) : 480 - 485
  • [26] Bias enhanced nucleation and growth of diamond films on titanium substrates
    Fehling, R
    Schreck, M
    Bergmaier, A
    Dollinger, G
    Stritzker, B
    TRENDS AND NEW APPLICATIONS OF THIN FILMS, 1998, 287-2 : 315 - 318
  • [27] Nucleation and growth of (100) textured diamond films in presence of nitrogen
    Li, Canhua
    Liao, Yuan
    Chang, Chao
    Wang, Guanzhong
    Fang, Rongchuan
    Wuli Xuebao/Acta Physica Sinica, 2000, 49 (09): : 1756 - 1763
  • [28] NUCLEATION AND INITIAL-STAGES OF GROWTH OF DIAMOND FILMS ON SILICON
    VAZQUEZ, L
    ALBELLA, JM
    SANCHEZ, O
    GOMEZALEIXANDRE, C
    MARTINEZDUART, JM
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (08): : 1103 - 1108
  • [29] NUCLEATION AND GROWTH OF DIAMOND FILMS ON ALUMINUM NITRIDE COATED NICKEL
    GODBOLE, VP
    JAGANNADHAM, K
    NARAYAN, J
    APPLIED PHYSICS LETTERS, 1995, 67 (09) : 1322 - 1324
  • [30] The nucleation and growth of (100) textured diamond films in presence of nitrogen
    Li, CH
    Liao, Y
    Chang, C
    Wang, GZ
    Fang, RC
    ACTA PHYSICA SINICA, 2000, 49 (09) : 1756 - 1763
12345