ANISOTROPIC FATIGUE HARDENING OF A NICKEL-BASE SINGLE-CRYSTAL AT ELEVATED-TEMPERATURE

被引：9

作者：

JABLONSKI, DA ^{[1
]}

SARGENT, S ^{[1
]}

机构：

[1] UNITED TECHNOL RES CTR,E HARTFORD,CT 06108

来源：

SCRIPTA METALLURGICA | 1981年 / 15卷 / 09期

关键词：

D O I：

10.1016/0036-9748(81)90243-X

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

页码：1003 / 1006

页数：4

共 50 条

[31] Microstructures of a single-crystal nickel-base superalloy after thermo-mechanical fatigue [J].

Wang, YC ;

Li, SX ;

Zhou, L ;

Ai, SH ;

Liu, F ;

Zhang, H ;

Wang, ZG .

PHILOSOPHICAL MAGAZINE, 2004, 84 (31) :3335-3351

[32] Crack appearance of single-crystal nickel-base superalloys after thermomechanical fatigue failure [J].

Zhang, J. X. ;

Harada, H. ;

Koizumi, Y. ;

Kobayashi, T. .

SCRIPTA MATERIALIA, 2009, 61 (12) :1105-1108

[33] ON THE EFFECT OF ORIENTATION ON CREEP-FATIGUE BEHAVIOR OF A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY [J].

RICHARDSFRANDSEN, R ;

TIEN, JK .

SCRIPTA METALLURGICA, 1984, 18 (07) :731-734

[34] THE EFFECT OF ORIENTATION ON THE CREEP-FATIGUE BEHAVIOR OF A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY [J].

RICHARDSFRANDSEN, R ;

COOPER, AH ;

TIEN, JK .

JOURNAL OF METALS, 1984, 36 (12) :80-80

[35] ASPECTS OF HIGH-TEMPERATURE LOW-CYCLE THERMOMECHANICAL FATIGUE OF A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY [J].

KRAFT, S ;

ZAUTER, R ;

MUGHRABI, H .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1993, 16 (02) :237-253

[36] EFFECT OF FREQUENCY ON ELEVATED TEMPERATURE FATIGUE OF NICKEL-BASE SUPERALLOY [J].

ORGAN, FE ;

GELL, M .

METALLURGICAL TRANSACTIONS, 1971, 2 (04) :943-&

[37] Low cycle fatigue damage in nickel-base superalloy single crystals at elevated temperature [J].

Fleury, E. ;

Remy, L. .

Materials Science and Engineering A, 1993, A167 (1-2) :23-30

[38] FATIGUE-CRACK PROPAGATION IN SINGLE-CRYSTAL CMSX-2 AT ELEVATED-TEMPERATURE [J].

ANTOLOVICH, BF ;

SAXENA, A ;

ANTOLOVICH, SD .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1993, 2 (04) :489-496

[39] Anisotropic Creep Rupture Properties of a Nickel-base Single Crystal Superalloy at High Temperature [J].

Shaohua ZhangJian Zhang and Langhong Lou Superalloys DivisionInstitute of Metal ResearchChinese Academy of SciencesShenyang China Shenyang National Laboratory for Materials ScienceInstitute of Metal ResearchChinese Academy of SciencesShenyang China .

JournalofMaterialsScience&Technology, 2011, 27 (02) :107-112

[40] Anisotropic Creep Rupture Properties of a Nickel-base Single Crystal Superalloy at High Temperature [J].

Zhang, Shaohua ;

Zhang, Jian ;

Lou, Langhong .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2011, 27 (02) :107-112

← 1 2 3 4 5 →