SYNTHESIS AND PROPERTIES OF NEW CRYSTALLINE POLY(ARYLENE ETHER NITRILES)

Crystalline poly (arylene ether nitrile) could be prepared by the polycondensation of 2,6-dihalobenzonitrile with resorcinol at 200-degrees-C in N-methylpyrrolidone in the presence of sodium carbonate. A reaction temperature of at least 200-degrees-C was necessary to attain high molecular weight polymer. Spectral data indicated that the polymer had the structure of a poly(meta-phenylene ether) with pendent nitrile groups on every other phenylene unit. Despite this structure, the crystallinity and the crystallization rate of the polymer were greater than those of the corresponding polymer with a para-linked structure. The glass transition temperature and the melting temperature of the polymer were almost the same as those of poly (etheretherketone) (PEEK(TM)). A series of other new poly(arylene ether nitriles) were also examined. The polymers derived from 4,4'-biphenol, dihydroxytetraphenylmethane, dihydroxydiphenylsulfone, and 1,5-isoquinolinediol had high glass transition temperatures. The poly(arylene ether nitriles) exhibited excellent tensile strength compared with the corresponding ketone- or sulfone-containing polymers. Comparing the three different kinds of polymers containing the same bisphenol units, the order of glass transition temperature was found to be sulfone- > nitrile- > ketone-containing polymers, while the order of tensile strength was nitrile- > ketone- > sulfone-containing polymers. The excellent mechanical properties are attributable to dipole-dipole interactions of nitrile groups. (C) 1993 John Wiley & Sons, Inc.