INFLUENCE OF SURFACE CONDITION AND ENVIRONMENT ON THE HYDRIDING OF TITANIUM

被引：32

作者：

COVINGTON, LC

机构：

来源：

CORROSION | 1979年 / 35卷 / 08期

关键词：

D O I：

10.5006/0010-9312-35.8.378

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper discusses the conditions under which cathodically impressed or galvanically induced currents can cause hydriding of titanium. The oxide film that normally covers the surface of titanium is shown to be an effective barrier to hydrogen penetration. In environments where this film is unstable or where the oxide film has been damaged by abrasion, hydrogen absorption can occur. Experimental evidence and service case histories are cited.

引用

页码：378 / 382

页数：5

共 14 条

[1]

BOYD JD, 1969, T ASM, V62, P977

[2] DIFFUSION OF TRITIUM IN RUTILE (TIO2) [J].

CASKEY, GR .

MATERIALS SCIENCE AND ENGINEERING, 1974, 14 (02) :109-114

[3]

CHARLOT LA, 1968, ELECTROCHEMICAL TECH, V6

[4]

COTTON JB, 1970, CHEM ENG PROG, V66, P57

[5]

COVINGTON LC, 1972, STP516 ASTM, P222

[6]

COVINGTON LC, 1977, METAL PROGR, V3, P38

[7]

COVINGTON LC, 1975, APR NACE CORR 75 TOR

[8]

JACOBS RL, 1972, TITANIUM TUBING EC S, V11, P33

[9] HYDRIDE HABIT PLANES IN TITANIUM-ALUMINUM ALLOYS [J].

PATON, NE ;

SPURLING, RA .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (11) :1769-1774

[10] HYDRIDE FORMATION DURING CATHODIC POLARIZATION OF TI .2. EFFECT OF TEMPERATURE AND PH OF SOLUTION ON HYDRIDE GROWTH [J].

PHILLIPS, II ;

POOLE, P ;

SHREIR, LL .

CORROSION SCIENCE, 1974, 14 (09) :533-542

← 1 2 →