A FATIGUE CRACK-GROWTH THRESHOLD

被引:27
|
作者
MARCI, G
机构
[1] Fracture and Mechanical Property Branch, Institute for Materials Research, DLR German Aerospace Research Establishment, D 5000 Köln 90
关键词
D O I
10.1016/0013-7944(92)90077-R
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
Fatigue crack growth (FCG) threshold has been determined on Ti6A14V, A1 7475-T7351, quenched and temepered steel 24CrMo4 as well as on the Ni-base alloys Inconel 617 and Nicrofer 5219 Nb. The main objective of the studies was to prove the transferability of the experimentally determined FCG threshold to service type fatigue loading. For FCG threshold testing, the following requirements must be fulfilled: (A) a FCG threshold has to be entirely above K(op); (B) a FCG threshold has to exist and has to be measured over the fatigue loading range K(max), i.e. K(max)* < K(max) < K(Ic); (C) a FCG threshold has to be the upper bound amplitude of cycles at a given K(max), the action of which does not produce FCG no matter how these threshold amplitudes are applied: (D) a FCG threshold must be a material parameter useful for material characterization and FCG design methodology under all fatigue loading conditions. It was shown that all the experimental procedures, i.e. type I, III and IV tests, furnished DELTA-K(T) values for A1 7475-T7351, Ti6A14V and the quenched and tempered steel 42CrMo4. The results suggest that this might be true for all A1 alloys, Ti alloys and steels. Therefore, any one test method can be used to determine DELTA-K(T) for these materials. The ASTM E 647 recommended procedure for threshold testing furnishes DELTA-K(T) values for these materials as well, if the R-ratio is equal to or higher than R(c). For the Ni-base alloys (Inconel 617 and Nicrofer 5219 Nb) only type III and IV tests can be used to determine a FCG threshold DELTA-K(T). This is due to the different behaviour of Ni-base alloys with respect to K(op).
引用
收藏
页码:367 / 385
页数:19
相关论文
共 50 条
  • [31] FATIGUE CRACK-GROWTH MODELING
    MCEVILY, AJ
    JOURNAL OF METALS, 1985, 37 (08): : A45 - A45
  • [32] MECHANISM OF FATIGUE CRACK-GROWTH
    LUKAS, P
    KUNZ, L
    KOVOVE MATERIALY-METALLIC MATERIALS, 1985, 23 (06): : 701 - 714
  • [33] FATIGUE CRACK-GROWTH IN POLYETHYLENE
    BUCKNALL, CB
    DUMPLETON, P
    POLYMER ENGINEERING AND SCIENCE, 1985, 25 (06): : 313 - 317
  • [34] FATIGUE CRACK-GROWTH RELIABILITY
    LAWRENCE, M
    LIU, WK
    BESTERFIELD, G
    BELYTSCHKO, T
    JOURNAL OF ENGINEERING MECHANICS, 1990, 116 (03) : 698 - 708
  • [35] A CRITICAL-STUDY OF THE CRACK CLOSURE EFFECT ON NEAR-THRESHOLD FATIGUE CRACK-GROWTH
    MINAKAWA, K
    NEWMAN, JC
    MCEVILY, AJ
    FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1983, 6 (04): : 359 - 365
  • [36] NEAR-THRESHOLD FATIGUE CRACK-GROWTH AND CRACK CLOSURE IN STEELS AND ALUMINUM-ALLOYS
    BLOM, AF
    JOURNAL OF METALS, 1983, 35 (08): : A25 - A25
  • [37] NEAR-THRESHOLD FATIGUE CRACK-GROWTH AND CRACK CLOSURE IN A NODULAR CAST-IRON
    OGAWA, T
    KOBAYASHI, H
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1987, 10 (04) : 273 - 280
  • [38] THE FATIGUE THRESHOLD AND CRACK-GROWTH BEHAVIOR OF MN-NI-AL BRONZES
    DICKSON, JI
    HANDFIELD, L
    BAILON, JP
    SAHOO, M
    CIM BULLETIN, 1984, 77 (866): : 42 - 42
  • [39] THRESHOLD AND LOW-RATE FATIGUE CRACK-GROWTH OF A NIMOV ROTOR STEEL
    SHIH, TT
    DONALD, JK
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1981, 103 (02): : 104 - 111
  • [40] THE EFFECT OF MICROSTRUCTURE ON THE THRESHOLD STRESS INTENSITY FOR FATIGUE CRACK-GROWTH IN POLYCRYSTALLINE COPPER
    MULLNER, H
    WEISS, B
    MATERIALS SCIENCE AND ENGINEERING, 1981, 48 (01): : 1 - 7