PRECIPITATION BEHAVIOR OF SULFIDES IN TI-ADDED ULTRA LOW-CARBON STEELS IN AUSTENITE

被引：67

作者：

YOSHINAGA, N

USHIODA, K

AKAMATSU, S

AKISUE, O

机构：

[1] Steel Research Laboratories, Nippon Steel Corporation, Shintomi, Futtsu, Chiba-ken

来源：

ISIJ INTERNATIONAL | 1994年 / 34卷 / 01期

关键词：

TIS; TI4C2S2; MNS; AUSTENITE; ULTRA LOW-CARBON STEEL; PRECIPITATION BEHAVIOR; SOLUBILITY PRODUCTS; TI-BEARING STEEL;

D O I：

10.2355/isijinternational.34.24

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The influences of S and Ti contents as well as slab reheating temperature on the precipitation behavior of sulfides in hot-rolled bands in Ti-added ultra low-carbon steels have been investigated. The results obtained are as follows: In the specimens with the same 0.02% Ti content, Ti4C2S2 decreases and TiS increases in number as S content increasses while in the specimens with the same 0.008% S content, TiS decreases and Ti4C2S2 increases in number as Ti content increases. The number of TiS increases when the slab reheating temperature is high. The solubility products of TiS and Ti4C2S2 in austenite have been also experimentally determined as follows: log[Ti][S]=-3 252/T-2.01 log[Ti][C](0.5)[S](0.5)=-5208/T-0.78 The experimental results above agree well with the results calculated using these solubility products. The reliability of solubility products determined in this study are checked and it is confirmed that the solubility products in this study is in good agreement with the published experimental results.

引用

页码：24 / 32

页数：9

共 26 条

[1]

CHINO H, 1965, SEITETSU KENKYU, P5817

[2]

Fukuda N., 1972, J JPN SOC TECHNOL PL, V13, P841

[3]

HAYAKAWA H, 1983, TETSU TO HAGANE, V69, pS594

[4]

HILIERTM, 1970, ACTA CHEM SCAND, V23, P3618

[5]

IRVINE KJ, 1967, J IRON STEEL I, V205, P161

[6] BAKE HARDENABILITY OF COLD-ROLLED TI-BEARING EXTRA LOW-CARBON STEEL SHEETS DUE TO PRECIPITATION CONTROL [J].

KAWASAKI, K ;

SANAGI, S ;

SENUMA, T ;

AKAMATSU, S ;

YOSHINAGA, N ;

AKISUE, O .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1993, 79 (01) :76-82

[7] OBSERVATION OF PRECIPITATES AND METALLOGRAPHIC GRAIN ORIENTATION IN STEEL BY A NON-AQUEOUS ELECTROLYTE-POTENTIOSTATIC ETCHING METHOD [J].

KUROSAWA, F ;

TAGUCHI, I ;

MATSUMOTO, R .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1979, 43 (11) :1068-1077

[8] CHARACTERIZATION OF TI CARBOSULFIDE PRECIPITATION IN TI MICROALLOYED STEELS [J].

LIU, WJ ;

YUE, S ;

JONAS, JJ .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10) :1907-1915

[9] GIBBS ENERGIES OF FORMATION OF TIS AND TI4C2S2 IN AUSTENITE [J].

LIU, WJ ;

JONAS, JJ ;

BOUCHARD, D ;

BALE, CW .

ISIJ INTERNATIONAL, 1990, 30 (11) :985-990

[10]

MIYOSHI T, 1992, CAMP ISIJ, V5, P862

← 1 2 3 →