AUTOMATED TORSION PENDULUM ANALYSIS OF THE FORMATION AND PROPERTIES OF A POLYPHTHALOCYANINE

被引:21
作者
GILLHAM, JK
机构
[1] Department of Chemical Engineering, Princeton University, Princeton, New Jersey
关键词
D O I
10.1002/pen.760190415
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The cure and transitions of a C10 diamide phthalocyanine resin have been investigated by the torsional braid method. Two relaxations (T′ > Tg and T > Tg) occurring above the glass transition temperature (Tg) are shown to correspond to two relaxations which develop prior to vitrification on isothermal cure. They bear directly on processibility of the material. Also investigated was the coupling between a low temperature transition (∼ − 146°C/2.1 Hz) inherent to the material and a low temperature water‐induced transition (∼ − 76°C/1.9 Hz). Copyright © 1979 Society of Plastics Engineers, Inc.
引用
收藏
页码:319 / 326
页数:8
相关论文
共 13 条
[1]  
BASCOM WD, 1976, HIGH PERFORMANCE COM, P15
[2]   INVESTIGATION OF T-11 (GREATER THAN TG) TRANSITION IN POLYSTYRENE BY TORSIONAL BRAID ANALYSIS [J].
GILLHAM, JK ;
BENCI, JA ;
BOYER, RF .
POLYMER ENGINEERING AND SCIENCE, 1976, 16 (05) :357-360
[3]   SEMIMICRO THERMOMECHANICAL TECHNIQUE FOR CHARACTERIZING POLYMERIC MATERIALS - TORSIONAL BRAID ANALYSIS [J].
GILLHAM, JK .
AICHE JOURNAL, 1974, 20 (06) :1066-1079
[4]  
GILLHAM JK, 1977, CHEM PROPERTIES CROS, P491
[5]  
GILLHAM JK, 1978, AM CHEM SOC ORG COAT, V38, P598
[6]  
GRIFFIN J, 1976, HABITATS HUMAINS ANT, P7
[7]  
GRIFFITH JR, 1974, AM CHEM SOC DIV ORG, V34, P446
[8]  
GRIFFITH JR, 1978, AM CHEM SOC DIV ORG, V38, P596
[9]  
GRIFFITH JR, 1974, ACS POLYM PREPR, V15, P787
[10]  
Walton T.R., 1975, ADHESION SCI TECHN B, V9B, P665