THE AGING OF AUSTENITIC FERRITIC STAINLESS-STEEL MOLDED AT TEMPERATURES BETWEEN 300-450-DEGREES-C OF LONG DURATION

被引：0

作者：

BONNET, S ^{[1
]}

BOURGOIN, J ^{[1
]}

GUTTMANN, D ^{[1
]}

GUTTMANN, M ^{[1
]}

机构：

[1] ELECT FRANCE,DEPT ETUD MAT,MORET,FRANCE

来源：

MEMOIRES ET ETUDES SCIENTIFIQUES DE LA REVUE DE METALLURGIE | 1987年 / 84卷 / 09期

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

页码：480 / 480

页数：1

共 50 条

[1] RELATIONSHIP BETWEEN SOLIDIFICATION AND MICROSTRUCTURE IN AUSTENITIC AND AUSTENITIC-FERRITIC STAINLESS-STEEL WELDS
SUUTALA, N
TAKALO, T
MOISIO, T
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (04): : 512 - 514
[2] HELIUM BUBBLE NUCLEATION AT 600-DEGREES-C IN A FERRITIC STAINLESS-STEEL
VONBRADSKY, G
GOODHEW, PJ
JOURNAL OF NUCLEAR MATERIALS, 1985, 135 (2-3) : 269 - 273
[3] STRUCTURE DEVELOPMENT OF AN AUSTENO-FERRITIC STAINLESS-STEEL BY HOLDING BETWEEN 600 AND 1150 DEGREES C
JOLLY, P
HOCHMANN, J
MEMOIRES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1973, 70 (02): : 117 - 124
[4] THE FRETTING WEAR OF NITROGEN-BEARING AUSTENITIC STAINLESS-STEEL AT TEMPERATURES TO 600-DEGREES
WATERHOUSE, RB
JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 1986, 108 (03): : 359 - 363
[5] AGING KINETICS OF CF3 CAST STAINLESS-STEEL IN TEMPERATURE-RANGE 300-DEGREES-C-400-DEGREES-C
PUMPHREY, PH
AKHURST, KN
MATERIALS SCIENCE AND TECHNOLOGY, 1990, 6 (03) : 211 - 219
[6] RELATIONSHIPS BETWEEN STRUCTURE AND MECHANICAL-PROPERTIES AT 20-DEGREES-C FOR THE A 286 AUSTENITIC STAINLESS-STEEL
LOIER, C
OTTMANN, MC
MEMOIRES ET ETUDES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1983, 80 (12): : 675 - 684
[7] EMBRITTLEMENT AND AGING AT 475-DEGREES-C IN AN EXPERIMENTAL FERRITIC STAINLESS-STEEL CONTAINING 38 WT-PERCENT CHROMIUM
CORTIE, MB
POLLAK, H
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 199 (02): : 153 - 163
[8] FAST-NEUTRON IRRADIATION HARDENING OF AUSTENITIC STAINLESS-STEEL AT 250-DEGREES-C
ELEN, JD
FENICI, P
JOURNAL OF NUCLEAR MATERIALS, 1992, 191 : 766 - 770
[9] HYDROGEN REDUCTION OF MOO3 AT TEMPERATURES BETWEEN 300 DEGREES AND 450 DEGREES C
HAWKINS, DT
WORRELL, WL
METALLURGICAL TRANSACTIONS, 1970, 1 (01): : 271 - &
[10] ATOM-PROBE STUDY OF PHASE-DECOMPOSITION OF FERRITE DURING AGING IN FERRITIC AUSTENITIC DUPLEX STAINLESS-STEEL
YOSHIMURA, T
ISHIKAWA, Y
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1992, 56 (08) : 873 - 880

← 1 2 3 4 5 →