PORE FORMATION DURING REACTIVE SINTERING OF EXTRUDED TITANIUM ALUMINUM POWDER MIXTURES

被引：0
|
作者：
DAHMS, M [1 ]
LEITNER, G [1 ]
POESSNECKER, W [1 ]
SCHULTRICH, S [1 ]
SCHMELZER, F [1 ]
机构：
[1] FRAUNHOFER EINRICHTUNG KERAM TECHNOL & SINTERWERKSTOFFE,O-8020 DRESDEN,GERMANY
来源：
ZEITSCHRIFT FUR METALLKUNDE | 1993年 / 84卷 / 05期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
A powder mixture Ti-49 at.% Al was extruded at room temperature. Swelling due to phase transformation during annealing was studied using differential scanning calorimetry and dilatometry. It is the result of several processes: (i) Kirkendall pores during solid state interdiffusion, (ii) macro-pores during the reaction of liquid aluminium and solid titanium, (iii) interdiffusion of Al3Ti and pure titanum forming the intermetallic phases gamma-TiAl and alpha2-Ti3Al. Swelling is anisotropic due to the elongated titanium particles. Sintering occurs at higher temperatures depending on the microstructure after Al3Ti formation. For technological applications, minimization of porosity is possible by optimization of the time - temperature path.
引用
收藏
页码：351 / 357
页数：7
相关论文
共 50 条
  • [1] Pore formation during reactive sintering of extruded titanium-aluminum powder mixtures
    Dahms, M.
    Leitner, G.
    Poessnecker, W.
    Schultrich, S.
    Schmelzer, F.
    Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1993, 84 (05): : 351 - 357
  • [2] TITANIUM ALUMINIDES BY HOT ISOSTATIC PRESSING OF COLD-EXTRUDED TITANIUM ALUMINUM POWDER MIXTURES
    DAHMS, M
    SEEGER, J
    SMARSLY, W
    WILDHAGEN, B
    ISIJ INTERNATIONAL, 1991, 31 (10) : 1093 - 1099
  • [3] Sintering of Titanium, Silicon, and Titanium Silicide Powder Mixtures
    G. A. Pribytkov
    M. I. Vagner
    V. V. Korzhova
    E. N. Korosteleva
    A. V. Gurskikh
    I. A. Firsina
    Powder Metallurgy and Metal Ceramics, 2014, 52 : 613 - 619
  • [4] Sintering of Titanium, Silicon, and Titanium Silicide Powder Mixtures
    Pribytkov, G. A.
    Vagner, M. I.
    Korzhova, V. V.
    Korosteleva, E. N.
    Gurskikh, A. V.
    Firsina, I. A.
    POWDER METALLURGY AND METAL CERAMICS, 2014, 52 (11-12) : 613 - 619
  • [5] Fabrication of unidirectional porous TiAl-Mn intermetallic compounds by reactive sintering using extruded powder mixtures
    Yang, SH
    Kim, WY
    Kim, MS
    INTERMETALLICS, 2003, 11 (08) : 849 - 855
  • [6] Influence of aluminum titanate formation on sintering of bimodal size-distributed alumina powder mixtures
    Taruta, Seiichi
    Itou, Yousuke
    Takusagawa, Nobuo
    Okada, Kiyoshi
    Otsuka, Nozomu
    1997, American Ceramic Soc, Westerville, OH, United States (80)
  • [7] Influence of aluminum titanate formation on sintering of bimodal size-distributed alumina powder mixtures
    Taruta, S
    Itou, Y
    Takusagawa, N
    Okada, K
    Otsuka, N
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1997, 80 (03) : 551 - 556
  • [8] SINTERING OF (ALUMINA + TITANIUM) POWDER MIXTURES AND ELABORATION OF THE CORRESPONDING CERMETS
    BRAICHOTTE, G
    CIZERON, G
    JOURNAL OF MATERIALS SCIENCE, 1989, 24 (09) : 3123 - 3136
  • [9] Sintering of (alumina + titanium) powder mixtures and elaboration of the corresponding cermets
    Braichotte, G., 1600, (24):
  • [10] Microstructure evolution of aluminum powder during sintering
    Key Laboratory of Mechanical Behavior and Design of Materials, Chinese Academy Sciences, Hefei 230026, China
    不详
    Cailiao Yanjiu Xuebao, 2008, 5 (473-478):
12345