LOW TEMPERATURE RECOVERY OF AL-ZN ALLOYS COLD-WORKED AT - 195DEGREES C

被引：3

作者：

CERESARA, S

机构：

[1] I.S.M.L., Novara

来源：

PHILOSOPHICAL MAGAZINE | 1968年 / 17卷 / 150期

关键词：

D O I：

10.1080/14786436808223205

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The resistivity recovery after cold-work at -195°C of a set of Al-Zn alloys, with Zn content ranging from 0 to 3.99 wt. %, is investigated by isochronal annealing procedure. Results agree with a previously discussed recovery model assuming vacancy migration in stage III. © 1968 Taylor & Francis Group, LLC.

引用

页码：1299 / &

共 50 条

[1] RECOVERY OF AL-SI ALLOYS COLD-WORKED AT-195 DEGREES C
SPRUSIL, B
FEDERIGHI, T
CERESARA, S
ACTA METALLURGICA, 1967, 15 (11): : 1762 - +
[2] RECOVERY OF DILUTE AL-SI ALLOYS COLD-WORKED AT -195 DEGREES C
HEGAZI, A
KOVACS, I
NAGY, E
PHYSICA STATUS SOLIDI, 1969, 33 (01): : 131 - &
[3] SMALL ANGLE X-RAY SCATTERING FROM COLD-WORKED AL-AG AND AL-ZN ALLOYS
JAN, JP
KOEHLER, JS
PHYSICAL REVIEW, 1954, 95 (02): : 665 - 666
[4] HIGH-TEMPERATURE STAGES IN RECOVERY SPECTRUM OF COLD-WORKED AL
HASLAR, V
VOSTRY, P
CZECHOSLOVAK JOURNAL OF PHYSICS, 1988, 38 (04) : 413 - 416
[5] RECOVERY OF COLD-WORKED ALUMINIUM AT LOW TEMPERATURES
HUTCHISON, TS
MCBRIDE, SL
PHYSICS LETTERS, 1962, 2 (03): : 157 - 159
[6] ON THE INTERPRETATION OF LOW-TEMPERATURE RECOVERY PHENOMENA IN COLD-WORKED METALS
NOWICK, AS
ACTA METALLURGICA, 1955, 3 (04): : 312 - 321
[7] THE EVOLUTION OF THE ENERGY STORED BY A GOLD-SILVER ALLOY COLD-WORKED AT 195-DEGREES-C AND AT ROOM TEMPERATURE
GREENFIELD, P
BEVER, MB
ACTA METALLURGICA, 1956, 4 (04): : 433 - 439
[8] RESISTIVITY RECOVERY OF COLD-WORKED DILUTE COPPER ALLOYS
PRITCHARD, C
PRATT, PL
ACTA CRYSTALLOGRAPHICA, 1960, 13 (12): : 1124 - 1124
[9] RECOVERY AND RECRYSTALLIZATION OF AN AL-0.18 WT PERCENT ZR ALLOY COLD-WORKED AT -196 DEGREES C
CERESARA, S
CONSERVA, M
FIORINI, P
MATERIALS SCIENCE AND ENGINEERING, 1972, 9 (01): : 19 - &
[10] RECOVERY PHENOMENA IN COLD-WORKED ALUMINIUM-ALUMINA ALLOYS
MISSIROLI, GF
NOBILI, D
ZIGNANI, F
JOURNAL OF NUCLEAR MATERIALS, 1967, 21 (02) : 199 - +

← 1 2 3 4 5 →