DEPTH DEPENDENCE OF ATOMIC MIXING BY ION-BEAMS

Ion backscattering spectrometry has been used to investigate the depth dependence of atomic mixing induced by ion beams. Samples consisting of a thin Pt (or Si) marker a few tens of angstroms thick buried at different depths in a deposited Si (or Pt) layer were bombarded with Xe+ of 300 keV at 2×1016 cm-2 dose and Ar+ of 150 keV at 5×1015cm-2 dose. Significant spreading of the marker was observed as a result of ion irradiation. The amount of spreading was measured as a function of depth of the marker, which was then compared with the deposited energy distribution. Measurements of this kind promise new insight into the nature of the interaction between ion beams and solids.