REVERSIBLE EMBRITTLEMENT IN ZIRCALOY-2

被引:8
作者
MAJUMDAR, P
SCULLY, JC
机构
[1] Department of Metallurgy, University of Leeds, Leeds
关键词
D O I
10.1016/0010-938X(79)90047-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
STRESS corrosion cracking in zircaloy-2 at room temperature has been reported by several authors1-3 who have observed cracking in Hg, CH3OH/I2, CH3OH/HC1 and aqueous NaC1. In the course of an extensive study of stress corrosion cracking in the zircaloy-2/CH3OH/HCI system a reversible embrittlement attributable to absorbed hydrogen has been observed and it is the purpose of this Short Communication to describe this phenomenon which has not been previously reported. © 1979.
引用
收藏
页码:141 / &
相关论文
共 4 条
[1]   ENVIRONMENTALLY INDUCED CRACKING OF ZIRCONIUM ALLOYS [J].
COX, B .
CORROSION, 1972, 28 (06) :207-&
[2]   ELECTROCHEMICAL FACTORS OF STRESS CORROSION CRACKING OF ZIRCONIUM IN CH3OH + HCL SOLUTION [J].
ELAYAPERUMAL, K ;
DE, PK ;
BALACHANDRA, J .
CORROSION SCIENCE, 1971, 11 (08) :579-+
[3]   STRESS CORROSION CRACKING OF TI AND ZR IN HCL-METHANOL SOLUTIONS [J].
MORI, K ;
TAKAMURA, A ;
SHIMOSE, T .
CORROSION, 1966, 22 (02) :29-&
[4]   STRESS-CORROSION CRACK-PROPAGATION IN A TI-O ALLOY IN AQUEOUS AND METHANOLIC SOLUTIONS [J].
SCULLY, JC ;
ADEPOJU, TA .
CORROSION SCIENCE, 1977, 17 (10) :789-812