METALLIC TEMPERATURE-DEPENDENCE OF RESISTIVITY IN HEAVILY-DOPED POLYACETYLENE BY NMR

H-1-NMR spin-lattice relaxation rate T-l(-1) of heavily doped polyacetylene was measured in an attempt to deduce the intrinsic resistivity of its metallic phase. Against our intention, in all of the samples a metallic behavior in the T-l(-1) expected for a quasi-one-dimensional metal was not found for some period after doping, and it was revealed that those T-l(-1)'s were governed by a relaxation mechanism due to residual Curie spins. In the bromine-doped sample, however, a change in the temperature dependence of T-l(-1) from the non-metallic behavior to the metallic one was found as time passed. It was confirmed that this change was caused by the partial substitution of hydrogen atoms by bromine atoms in the polyacetylene chain. We succeeded in deducing the temperature dependence of intrinsic resistivity for metallic polyacetylene from the data of T-l(-1).