STUDY ON THE EFFECT OF DECORATION OF CARBON VACANCY PAIRS BY CARBON-ATOMS IN QUENCHED ALPHA-FE AND CR 25-PERCENT-TYPE STEEL ALLOY BY MAGNETIC MEASUREMENTS

被引：3
作者：
ALI, AR
FARID, Z
FAHIM, MA
GHOBRIAL, FZ
机构：
[1] Physics Department, Faculty of Science, Cairo University, Giza
来源：
PHYSICA STATUS SOLIDI A-APPLIED RESEARCH | 1994年 / 143卷 / 01期
关键词：
D O I：
10.1002/pssa.2211430105
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Quenching experiments are carried out on alpha-Fe and Cr 25%-type steel alloy by using magnetic susceptibility, magnetic coercivity, and magnetic anisotropy. A value of (0.75 +/- 0.05) eV is determined for the carbon-vacancy binding energy. Two recovery stages are observed after quenching in the temperature range 75 to 500-degrees-C. The first stage is inferred to the decoration of carbon vacancy pairs with carbon atoms with the possible dissociation of polycarbon-vacancy complexes by spitting-off of carbon atoms at higher annealing temperatures. The second annealing stage is attributed to the formation of precipitated cementite particles by nucleation of carbon atoms released from polycarbon vacancy complexes and the subsequent dissociation of carbon vacancy pairs at higher annealing temperatures.
引用
收藏
页码：35 / 49
页数：15
相关论文
共 21 条
[1]  
ALI AR, 1990, J MATER SCI, V25, P1468
[2]   STUDY ON THE RECOVERY OF LATTICE-DEFECTS IN COLD-WORKED NI-5 WT-PERCENT MN BY DISLOCATION PINNING AND MAGNETIC COERCIVITY [J].
ALI, AR ;
FARID, ZM ;
TAKLA, E .
PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1992, 129 (01) :87-99
[3]   KINETICS OF CARBON PRECIPITATION IN IRRADIATED IRON- .3. CALORIMETRY [J].
ARNDT, RA ;
DAMASK, AC .
ACTA METALLURGICA, 1964, 12 (04) :341-&
[4]   ANNEALING OF VACANCIES AND AGING IN AL-LI ALLOYS [J].
CERESARA, S ;
GIARDA, A ;
SANCHEZ, A .
PHILOSOPHICAL MAGAZINE, 1977, 35 (01) :97-110
[5]  
CHIKAZUMI S, 1964, PHYS MAGNETISM, P263
[6]  
DAMASK A, 1965, AM SOC METALS, P317
[7]  
DAMASK AC, 1963, POINT DEFECTS METALS, P145
[8]   THE INFLUENCE OF SMALL AMOUNTS OF INTERSTITIAL SOLUTE ATOMS ON THE DETERMINATION OF THE ACTIVATION-ENERGIES FOR SELF-DIFFUSION AND VACANCY FORMATION IN ALPHA-IRON [J].
DESCHEPPER, L ;
KNUYT, G ;
STALS, LM .
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 1981, 67 (01) :153-162
[9]  
FRANK W, 1986, INT C VACANCIES INTE, P82
[10]  
GHAZI WAKILI K, 1990, Z PHYS B CON MAT, V79, P39, DOI 10.1007/BF01387823
123