CREEP CRACK-GROWTH IN A 1-PERCENT-CRMOV STEEL AND A 32-PERCENT-NI-20-PERCENT-CR ALLOY

被引：1

作者：

HOLLSTEIN, T ^{[1
]}

WEBSTER, GA ^{[1
]}

DJAVANROODI, F ^{[1
]}

机构：

[1] UNIV LONDON IMPERIAL COLL SCI TECHNOL & MED,DEPT MECH ENGN,LONDON SW7 2BX,ENGLAND

来源：

MATERIALS AT HIGH TEMPERATURES | 1992年 / 10卷 / 02期

关键词：

CREEP; CRACK GROWTH; NICR ALLOY;

D O I：

10.1080/09603409.1992.11689406

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The creep crack growth behaviour of two high-temperature materials has been determined in 25 laboratories within the European Group on Fracture (EGF). This paper presents a summary of these round-robin tests on the 'measurement of crack growth under high temperature conditions'. It is shown that the most satisfactory correlations of creep crack growth rates are achieved with the creep fracture mechanics parameter C*. Little influence of specimen shape and size is observed and it is demonstrated that the specimen deformation and cracking behaviour occurs under plane stress conditions.

引用

页码：92 / 96

页数：5

共 50 条

[1] CREEP CRACK-GROWTH AND CAVITATION DAMAGE IN A 12-PERCENT CRMOV STEEL
WIESNER, C
EARTHMAN, JC
EGGELER, G
ILSCHNER, B
ACTA METALLURGICA, 1989, 37 (10): : 2733 - 2741
[2] CREEP DEFORMATION IN 20 PERCENT CR-35 PERCENT NI STEEL
MODEER, B
LAGNEBOR.R
JERNKONTORETS ANNALER, 1971, 155 (07): : 363 - &
[3] CHARACTERIZATIONS OF CREEP CRACK-GROWTH IN 1-PERCENT CR MO V STEEL
SMITH, DJ
WEBSTER, GA
JOURNAL OF STRAIN ANALYSIS FOR ENGINEERING DESIGN, 1981, 16 (02): : 137 - 143
[4] INTERNAL OXIDATION OF AN 18 PERCENT CR-11 PERCENT NI COMMERCIAL STEEL AND A 20 PERCENT CR-11 PERCENT NI ALLOY
ERICSSON, T
TIDSSKRIFT FOR KJEMI BERGVESENOG METALLURGI, 1969, 29 (12): : 216 - &
[5] NBC PRECIPITATION IN A 20 PERCENT CR - 25 PERCENT NI - 1 PERCENT NB AUSTENITIC STEEL
RAMASWAMY, V
WEST, DRF
JOURNAL OF THE IRON AND STEEL INSTITUTE, 1970, 208 : 391 - +
[6] FRACTURE-MECHANICS AND CREEP CRACK-GROWTH OF 1-PERCENT-CR-1/2-PERCENT-MO STEEL WITH AND WITHOUT PRIOR EXPOSURE TO CREEP CONDITIONS
VANLEEUWEN, HP
SCHRA, L
ENGINEERING FRACTURE MECHANICS, 1987, 27 (04) : 483 - &
[7] EFFECTS OF TEMPERATURE AND ENVIRONMENT ON FATIGUE CRACK-GROWTH MECHANISMS IN A 9-PERCENT CR 1-PERCENT-MO STEEL
COTTERILL, PJ
KNOTT, JF
ACTA METALLURGICA ET MATERIALIA, 1992, 40 (10): : 2753 - 2764
[8] PRECIPITATION IN A 20 PERCENT CR - 25 PERCENT NI STEEL STABILIZED WITH NIOBIUM
SUMERLING, R
NUTTING, J
JOURNAL OF THE IRON AND STEEL INSTITUTE, 1965, 203 : 398 - &
[9] OVERLOAD RETARDATION OF FATIGUE CRACK-GROWTH IN A 9-PERCENT-CR 1-PERCENT-MO STEEL AT ELEVATED-TEMPERATURES
COTTERILL, PJ
KNOTT, JF
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1993, 16 (01) : 53 - 70
[10] SOLUBILITY OF NBC IN 20 PERCENT CR-25 PERCENT NI STAINLESS STEEL
DEIGHTON, M
JOURNAL OF THE IRON AND STEEL INSTITUTE, 1967, 205 : 535 - &

← 1 2 3 4 5 →