REINFORCEMENT OF SILICONE ELASTOMER BY FINE PARTICLES

被引：9
作者：
BAKER, D
CHARLESBY, A
MORRIS, J
机构：
[1] Physics Department, Royal Military College of Science, Shrivenham, Wilts
来源：
POLYMER | 1968年 / 9卷 / 08期
关键词：
D O I：
10.1016/0032-3861(68)90053-0
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
The elastic modulus of silicone elastomers is greatly enhanced by the presence of fine particles (fillers). Exposure to high energy radiation offers a convenient method of introducing crosslinks in a quantitative manner. It is found that for a wide range of filler particles there is little linking between polymer and filler. The increase in modulus is proportional to dose (i.e. crosslink density) and to filler concentration, and is usually independent of the nature of the filler surface. However, it is inversely proportional to filler diameter. It is concluded that the increase is due primarily to physical interference of the filler particles with elastic deformation of the network. © 1968.
引用
收藏
页码：437 / +
页数：1
相关论文
共 19 条
  • [1] THE RUPTURE PROCESS IN CARBON-LOADED RUBBERS - AN ELECTRON-MICROSCOPIC INVESTIGATION
    ANDREWS, EH
    WALSH, A
    [J]. JOURNAL OF POLYMER SCIENCE, 1958, 33 (126): : 39 - 52
  • [2] [Anonymous], REINFORCEMENT ELASTO
  • [3] TENSILE STRENGTH OF FILLED GR-S VULCANIZATES
    BUECHE, F
    [J]. JOURNAL OF POLYMER SCIENCE, 1958, 33 (126): : 259 - 271
  • [4] ANALYSIS OF THE SOLUBILITY BEHAVIOUR OF IRRADIATED POLYETHYLENE AND OTHER POLYMERS
    CHARLESBY, A
    PINNER, SH
    [J]. PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1959, 249 (1258): : 367 - 386
  • [5] CHARLESBY A, 1959, P ROY SOC A, V230, P120
  • [6] Fricke H, 1929, PHILOS MAG, V7, P129
  • [7] GUTH E, 1938, PHYS REV, V52, P322
  • [8] HARRIS JO, 1965, REINFORCEMENT ELASTO, P268
  • [9] KRAUS G, 1965, REINFORCING ELASTOME, P69
  • [10] KRAUS G, 1965, REINFORCEMENT ELA ED, P268
12