POLYTYPIC STRUCTURES IN CLOSE-PACKED ZR(FECR)2 LAVES PHASES

被引:5
|
作者
BURANY, XM [1 ]
NORTHWOOD, DO [1 ]
机构
[1] UNIV WINDSOR,ENGN MAT GRP,WINDSOR N9B 3P4,ONTARIO,CANADA
来源
JOURNAL OF THE LESS-COMMON METALS | 1991年 / 170卷 / 01期
关键词
D O I
10.1016/0022-5088(91)90047-8
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The polytypic structures formed in bulk Zr(Fe(1-x)Cr(x))2 alloys (x = 0 to 1) in the as-cast and heat-treated conditions (30 min at 850 or 900-degrees-C) were determined by electron diffraction techniques, ZrCr2 was the only bulk alloy to exhibit a range of polytypic structures. The hexagonal polytypes 2H, 4H, 8H and 12H were present in as-cast ZrCr2. Upon heat treatment at 850 or 900-degrees-C the hexagonal polytypes were replaced with the cubic polytype 3R and 3R-twinned. The cubic polytype 3R was the only structure formed in as-cast or heat-treated ZrFe2. The hexagonal polytype 2H was the only structure formed in Zr(Fe(1-x)Cr(x)), alloys (x = 0.25, 0.45 and 0.75) in all metallurgical conditions. This behaviour is compared with that of Zr(Fe(1-x)Cr(x))2(x not-equal-to 1) precipitates in zirconium-rich alloys where a variety of polytypes are observed. The presence of the polytype structures in the precipitates is attributed to the lattice misfit and associated distortional stresses present between the precipitates and the alpha-Zr matrix in the Zr-rich alloys. No such stresses would be present in the bulk alloys.
引用
收藏
页码:27 / 35
页数:9
相关论文
共 50 条
  • [31] Identifying close-packed planes in complex crystal structures
    Kelly, P. M.
    Ren, H. -P.
    Qiu, D.
    Zhang, M. -X.
    ACTA MATERIALIA, 2010, 58 (08) : 3091 - 3095
  • [32] CLUSTERS OF INERT-GASES OF THE CLOSE-PACKED STRUCTURES
    SMIRNOV, BM
    PHYSICA SCRIPTA, 1995, 52 (06): : 710 - 717
  • [33] X-RAY-ANALYSIS OF CLOSE-PACKED STRUCTURES
    MARDIX, S
    PHASE TRANSITIONS, 1993, 43 (1-4) : 49 - 56
  • [34] ARGYRODITES - NEW FAMILY OF TETRAHEDRALLY CLOSE-PACKED STRUCTURES
    KUHS, WF
    NITSCHE, R
    SCHEUNEMANN, K
    MATERIALS RESEARCH BULLETIN, 1979, 14 (02) : 241 - 248
  • [35] A CONDENSED WAY OF REPRESENTING INORGANIC CLOSE-PACKED STRUCTURES
    LIMADEFARIA, J
    ZEITSCHRIFT FUR KRISTALLOGRAPHIE KRISTALLGEOMETRIE KRISTALLPHYSIK KRISTALLCHEMIE, 1965, 122 (5-6): : 346 - +
  • [36] DOMAIN-STRUCTURES OF TETRAHEDRALLY CLOSE-PACKED PHASES WITH JUXTAPOSED PENTAGONAL ANTIPRISMS .1. STRUCTURE DESCRIPTION AND HREM IMAGES OF THE C-14 LAVES AND MU-PHASES
    YE, HQ
    LI, DX
    KUO, KH
    PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1985, 51 (06): : 829 - 837
  • [37] THE DIFFRACTION OF X-RAYS BY CLOSE-PACKED POLYTYPIC CRYSTALS CONTAINING SINGLE STACKING-FAULTS .2. THEORY FOR HEXAGONAL AND RHOMBOHEDRAL STRUCTURES
    MICHALSKI, E
    KACZMAREK, S
    DEMIANIUK, M
    ACTA CRYSTALLOGRAPHICA SECTION A, 1988, 44 : 650 - 657
  • [38] First-principles structures for the close-packed and the 7/2 motif of collagen
    Jalkanen, Karl J.
    Olsen, Kasper
    Knapp-Mohammady, Michaela
    Bohr, Jakob
    EPL, 2012, 100 (02)
  • [39] CENTROSYMMETRIC SPACE GROUPS IN CLOSE-PACKED MX2-TYPE STRUCTURES
    JAIN, PC
    TRIGUNAYAT, GC
    ACTA CRYSTALLOGRAPHICA SECTION A, 1977, 33 (MAR1): : 255 - 256
  • [40] Structural stability of Fe-based topologically close-packed phases
    Ladines, A. N.
    Hammerschmidt, T.
    Drautz, R.
    INTERMETALLICS, 2015, 59 : 59 - 67