POLYSULFONE AND POLY(PHENYLENE SULFIDE) BLENDS .1. THERMAL CHARACTERIZATION AND PHASE MORPHOLOGY

The phase behaviour and morphology of injection moulded specimens of polysulphone (PSF) and poly(phenylene sulphide) (PPS) blends were studied by differential scanning calorimetry (d.s.c.), dynamical mechanical thermal analysis (d.m.t.a.) and transmission electron microscopy (TEM). The blends are phase separated regardless of the blend composition as revealed by d.s.c., d.m.t.a. and TEM. Upon annealing at 160°C for 2 h, d.m.t.a. results indicate that the PPS phase remains in the amorphous state at compositions <10%. At compositions between 20 and 35%, the PPS appears to be dispersed in a mixed mode of amorphous and crystalline domains. Above 35% the PPS phase appears to become fully crystallized upon annealing of the blends. At 10% PPS, TEM results showed 35-200 nm size dispersion both in the as-moulded and in the annealed specimens. At 20% the PPS phase varied widely in size, from 35 nm to tens of micrometres but remained as an included phase. TEM also revealed a compound morphology of the included phase at a composition of 50 wt% of each component. © 1990.