TERNARY PHASE-EQUILIBRIA IN THE ZR-SI-C SYSTEM

被引：15

作者：

WANG, YZ ^{[1
]}

CARIM, AH ^{[1
]}

机构：

[1] PENN STATE UNIV,DEPT MAT SCI & ENGN,UNIVERSITY PK,PA 16802

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1995年 / 78卷 / 03期

关键词：

D O I：

10.1111/j.1151-2916.1995.tb08229.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Phase equilibria in the ternary Zr-Si-C system at 1200 degrees C are investigated in this work, A specific effort was made to fabricate a stable or metastable Zr3SiC2 phase, analogous to Ti3SiC2, but no evidence of such a compound was observed, The existence of the Zr5Si4 and Zr3Si phases, which were previously described in analyses of the Zr-Si binary, is confirmed in this study and their phase relationships within the ternary Zr-Si-C system are established by electron microprobe analysis and transmission electron microscopy.

引用

页码：662 / 666

页数：5

共 17 条

[1]

ARUNAJATESAN S, 1994, THESIS PENNSYLVANIA

[2]

ARUNAJATESAN S, 1995, IN PRESS J AM CERAM

[3] REACTIONS OF REFRACTORY SILICIDES WITH CARBON AND NITROGEN [J].

BREWER, L ;

KRIKORIAN, O .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1956, 103 (01) :38-51

[4]

BRUKL CE, 1966, AFML TR652 AIR FOR 2, V10

[5]

KARPINSK.OG, 1966, ACTA CRYSTALLOGR, VS 21, pA82

[6]

KUBASCHEWSKI O, 1983, ATOM ENERGY REV, P165

[7]

LUNDIN CE, 1953, T AM SOC METAL, V45, P901

[8]

MOKOZUMI S, 1985, J MATER SCI, V20, P3976

[9]

Nowotny H., 1956, MONATSH CHEM, V87, P447

[10]

Okamoto H., 1990, B ALLOY PHASE DIAGRA, V11, P513, DOI 10.1007/BF02898272

← 1 2 →