DISPERSION POLYMERIZATION OF STYRENE IN ETHANOL - MONOMER PARTITIONING BEHAVIOR AND LOCUS OF POLYMERIZATION

A thermodynamic model has been proposed for the simulation of monomer partitioning behavior in the dispersion polymerization of styrene in ethanol. The monomer concentration in the polymer particles is very low (20 vol% at 5% conversion) and decreases further as the polymerization proceeds. It is independent of stabilizer concentration but is strongly dependent on initial monomer concentration. The partition coefficient of styrene increases from 0. 8 to 1. 1 with increasing conversion. There are two polymerization loci in dispersion polymerization, namely the continuous and polymer phases. Competition between solution and heterogeneous polymerization has been observed in this system. The rate of dispersion polymerization is dependent on initial monomer concentration but is independent of initiator concentration at higher conversions. The molecular weight of the polymers produced by this process increases with increasing conversion and decreases with increasing initiator concentration.