ND-FE-B-BASED MAGNETS - MAGNETIC-PROPERTIES AND MICROSTRUCTURAL APPEARANCE WITH COPPER ADDITION

被引：10
作者：
KNOCH, KG [1 ]
KIANVASH, A [1 ]
HARRIS, IR [1 ]
机构：
[1] UNIV TABRIZ,FAC ENGN,TABRIZ,IRAN
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 1992年 / 183卷
关键词：
D O I：
10.1016/0925-8388(92)90730-W
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The microstructure of sintered permanent magnets with a composition 17Nd-76.5Fe-5B-1.5Cu was investigated by optical microscopy, electron probe microanalysis and transmission electron microscopy. Using the hydrogen decrepitation processing route, maximum magnetic properties of H(cJ) = 950 kA m- 1 and (BH)max = 230 kJ m-3 were obtained after high temperature homogenization and low temperature annealing. The main effect of the heat treatment procedure was to change the proportion of phases in the four phase microstructure. In addition to PHI and a neodymium-rich phase, two new phases were found: an Nd1Cu1-type phase and a phase Nd30Fe65Cu5. The latter seems to play an important role in obtaining high coercivity.
引用
收藏
页码：54 / 58
页数：5
相关论文
共 11 条
  • [1] Allibert C. H., 1989, CONCERTED ACTION MAG, P358
  • [2] ANALYTICAL TEM STUDY OF AL-DOPED, 2-PHASE ND-FE-B SINTERED MAGNETS
    FIDLER, J
    KNOCH, KG
    KRONMULLER, H
    SCHNEIDER, G
    [J]. JOURNAL OF MATERIALS RESEARCH, 1989, 4 (04) : 806 - 814
  • [3] FIDLER J, 1990, 6TH INT S MAGN AN CO, P176
  • [4] DIFFUSION-ALLOYED ADDITIVES IN DIE-UPSET ND-FE-B MAGNETS
    FUERST, CD
    BREWER, EG
    [J]. JOURNAL OF APPLIED PHYSICS, 1991, 69 (08) : 5826 - 5828
  • [5] KIANVASH A, 1991, 5TH JOINT MMM INT C
  • [6] KNOCH KG, IN PRESS
  • [7] KWON HW, 1991, 5TH JOINT MMM INT C
  • [8] MAGNETIC-PROPERTIES OF SINTERED PERMANENT-MAGNETS - PR-FE-CU-B, ND-FE-CU-B
    LIN, CH
    CHEN, CJ
    WU, CD
    CHANG, WC
    CHEN, SK
    CHIN, TS
    [J]. IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) : 2607 - 2609
  • [9] MUKAI T, 1990, 11TH P INT WORKSH RA, P72
  • [10] OHKI T, 1989, 10TH P INT WORKSH RA, P399
12