FABRICATION OF ZIRCONIA-ALUMINA FUNCTIONALLY GRADIENT MATERIAL BY SUPERPLASTIC DIFFUSION BONDING

被引：22

作者：

NAGANO, T ^{[1
]}

WAKAI, F ^{[1
]}

机构：

[1] GOVT IND RES INST,DEPT CERAM SCI,KITA KU,NAGOYA,AICHI 462,JAPAN

来源：

JOURNAL OF MATERIALS SCIENCE | 1993年 / 28卷 / 21期

关键词：

D O I：

10.1007/BF00365183

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Functionally gradient ZrO2-Al2O3 material was fabricated by superplastic diffusion bonding in the present study. Conditions included a bonding temperature of 1550-degrees-C, a time of 30 min, and strains of 17, 33 and 50%. Complete bonding was obtained under all of these bonding conditions. The apparent bending strength of functionally gradient material fabricated by superplastic diffusion bonding was 1860 MPa at the strain of 50%.

引用

页码：5793 / 5799

页数：7

共 18 条

[1] FUKUSHIMA T, 1990, 1ST P INT S FUNCT GR, P145
[2] MIYAMOTO Y, 1990, 1ST P INT S FUNCT GR, P257
[3] DIFFUSION BONDING OF CERAMICS - MULLITE, ZRO2-TOUGHENED MULLITE
NAGANO, T
KATO, H
WAKAI, F
[J]. JOURNAL OF MATERIALS SCIENCE, 1991, 26 (18) : 4985 - 4990
[4] DIFFUSION BONDING OF ZIRCONIA ALUMINA COMPOSITES
NAGANO, T
KATO, H
WAKAI, F
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (11) : 3476 - 3480
[5] NAGANO T, 1989, P MRS INT M ADV MATE, V7, P285
[6] NASLAIN R, 1990, 1ST P INT S FUNCT GR, P91
[7] NASLAIN R, 1990, 1ST P INT C FUNCT GR, P71
[8] PANDA PC, 1988, J AM CERAM SOC, V71, pC507, DOI 10.1111/j.1151-2916.1988.tb05820.x
[9] SASAKI M, 1990, 1ST P INT S FUNCT GR, P231
[10] SASAKI M, 1990, 1ST P INT S FUNCT GR, P83

← 1 2 →